利用燃气风洞模拟系统对三维C/SiC复合材料的持久寿命进行了考核,并分析了温度(1 200～1 500℃)和应力(100,240 MPa)对持久寿命的影响.结果表明:随温度升高,该复合材料内应力状态的改变、基体氧化生成SiO2对裂纹的封填以及基体裂纹变窄三种因素共同作用加强,使得复合材料的持久寿命延长;应力越大,复合材料中基体裂纹宽度越大,数量越多,造成复合材料损伤加剧,持久寿命缩短.
参考文献
| [1] | 张立同,成来飞.连续纤维增韧陶瓷基复合材料可持续发展战略探讨[J].复合材料学报,2007(02):1-6. |
| [2] | Hui Mei;Laifei Cheng;Xingang Luan .Simulated Environments Testing System for Advanced Ceramic Matrix Composites[J].International journal of applied ceramic technology,2006(3):252-257. |
| [3] | Ludovic QUEMARD;Francis REBILLAT;Alain GUETTE .Degradation mechanisms of a SiC fiber reinforced self-sealing matrix composite in simulated combustor environments[J].Journal of the European Ceramic Society,2007(1):377-388. |
| [4] | Xu Y.;Zhang L. .Oxidation behavior of three-dimensional SiC/SiC composites in air and combustion environment[J].Composites, Part A. Applied science and manufacturing,2000(9):1015-1020. |
| [5] | 张钧,徐永东,张立同,成来飞,董宁.3D C/SiC复合材料基体裂纹间距分布规律[J].航空材料学报,2003(03):11-14. |
| [6] | 罗国清 .3D-C/SiC复合材料的拉伸性能[D].西北工业大学,2003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%