采用直接沉淀法制备了TiO2-CeO2纳米复合氧化物,分析了不同铈钛摩尔比、pH和不同反应温度对合成复合氧化物及其紫外屏蔽效果的影响。研究结果表明,采用直接沉淀法制得了面心立方结构CeO2和锐钛矿型的TiO2混合物,铈钛摩尔比为0.4时复合氧化物在250～450nm波段之间有良好的紫外屏蔽性能。
A series of nanometer sized TiO2-CeO2 composites were prepared by the direct-precipitation method.The effects of Ce/Ti ratio,pH value and reaction temperature on the resultant composites and their UV-shielding properties were investigated.The results show that the prepared nanoparticles are consisted of face-centered cubic CeO2 and anatase TiO2.Good UV-shielding performance was achieved with a Ce/Ti molar ratio of 0.4 in the UV region of 245 nm to 450 nm.
参考文献
| [1] | 李曦,刘连利,王莉莉.纳米二氧化硅的研究现状与进展[J].渤海大学学报（自然科学版）,2006(04):304-308. |
| [2] | 朱兆武,龙志奇,崔大立,张顺利,张国成.超细CeO2粉体的制备及其紫外线吸收性能[J].中国有色金属学报,2005(03):435-440. |
| [3] | 陈忠伟,余爱萍,罗美芳,方图南,古宏晨.抗紫外纳米ZnO粉体的表面改性与脂肪酸改性机理探讨[J].化学世界,2002(05):227-229,232. |
| [4] | 崔爱莉,王亭杰,金涌.SiO2和Al2O3在TiO2表面的成核包覆与成膜包覆[J].化工冶金,1999(02):178-181. |
| [5] | 梁飞雪,朱华青,秦张峰,王辉,王国富,王建国.CeO2-TiO2复合氧化物的制备、表征及其对CO氧化的催化性能[J].催化学报,2008(03):264-268. |
| [6] | 陈林深,吕光烈,胡秀荣.中温制备CeO2-TiO2复合氧化物及其结构研究[J].中国稀土学报,2001(04):334-337. |
| [7] | 李玉,韩兆让,翟永爱,刘春丽,余娜,崔琳琳,陈延亮.TiO2/SiO2复合材料的制备与表征[J].化学研究,2007(01):19-22. |
| [8] | 马琦,张保住,张志强,任建国,张智敏.CeO2-TiO2复合光催化剂的制备及日光催化研究[J].应用化工,2005(03):153-155. |
| [9] | 董玉红,赵青南,马鸣明,汪振东.溶胶-凝胶法制备玻璃表面CeO2-TiO2紫外吸收薄膜的研究[J].中国稀土学报,2009(03):399-403. |
| [10] | Anderson C;Bard AJ .Improved photocatalytic activity and characterization of mixed TiO2/SiO2 and TiO2/Al2O3,materials[J].journal of Physical Chemistry B,1997,101(14):2611-2616. |
| [11] | 刘桂霞,孙多先,洪广言.阳离子聚氨酯/CeO2纳米复合材料的制备[J].应用化学,2003(03):266-268. |
| [12] | V.C法默.矿物的红外光谱[M].北京:科学出版社,1982 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%