通过光学金相和扫描电镜观察,分析了Ti-46.5Al-2.5V-1.0Cr(at.%)合金中添加微量稀土Gd对其铸态和变形组织的影响.结果表明,含Gd的TiAl合金其铸造组织晶粒更细小,变形宏观组织中均匀变形区较大,变形组织中动态再结晶的体积分数高,层片分解较完全.
参考文献
| [1] | Yamaguchi M .High-Temperatures Structural Intermetallies[J].Acta Materialia,2000,48:307. |
| [2] | Young-won Kim.Intermetallic Alloys Based on Gamma Titanium Aluminide[J].JOM-Journal of the Minerals Metals and Materials Society,1989:24. |
| [3] | 李臻熙,曹春晓.添加微量硼对TiAl合金持久性能的影响[J].中国有色金属学报,2005(06):836-841. |
| [4] | Takahashi T .Alloying Effect of Vanadium on the Stucture and Strength of γ-Phase Titanium Aluminides With AluminumRich Compositions[J].Materials Science and Engineering,1997,A239-240:271. |
| [5] | Ji Zhang .Microstructure Preparation and Hot-Deformation of Ti-46.2Al-2.0V-1.0Cr-0.3Ni Alloy[J].Intermetallics,2000,8:321. |
| [6] | Y. Wu;K. Hagihara;Y. Umakoshi .Influence of Y-addition on the oxidation behavior of Al-rich gamma-TiAl alloys[J].Intermetallics,2004(5):519-532. |
| [7] | Fu-Sheng Sun;Chun-Xiao Cao;Seung-Eon Kim .EFFECT OF Nd ON THE MICROSTRUCTURE AND PROPERTIES OF A TiAl ALLOY[J].Scripta materialia,2001(12):2775-2780. |
| [8] | Sun Y;Zhang Z;Xue F et al.Effect of Cerium Addition on Tensile Properties of Fe3 Al-Based Alloy at Ambient Temperature[J].Journal of Materials Science Letters,1996,15:820. |
| [9] | Chung C Y;Xie C Y;Hsu T Y .Effect of Rare EarthNdon the Ductility and Fracture Behaviour of A Ni-Rich Nial Alloy[J].Scripta Materialia,1997,37:99. |
| [10] | Xia K .Effects of Gd Addition,Lamellar Spacing and Loading Direction on Creep Behaviour of a Fully Lamellar Ti-44Al1Mn-2.5Nb Alloy[J].Acta Materialia,2004,52:841. |
| [11] | Li W .Microstructure Observations in Rare Earth Element Gd-Modified Ti-44at%Al[J].Intermetallics,2000,8:519. |
| [12] | Hishinuma A .Development and Tensile Properties of Ti40Al-10V Alloy[J].INTERMETALLICS,1999,7:875. |
| [13] | Liu C T .Microstructures and Properties of a Hot-Extruded TiAI Containing no Cr[J].Materials Science and Engineering,2002,A329-A331:416. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%