Dry sliding friction between the Al59Cu25.5Fe12.5B3 quasicrystals (QCs)/coating of the diamond-like carbon (DLC) was carried out by self-made tribometer under different conditions. The influences of four parameters (temperature, sliding velocity, applied load, atmosphere) on friction and wear of quasicrystal surface were studied. Microstructure of quasicrystal, morphology of worn surface, and wear debris were observed by scanning electron microscopy (SEM).The results showed that for QCs, the friction coefficient and roughness of worn surface were influenced by the parameters, especially greatly by the temperature. With rise of the applied load and sliding velocity, the friction coefficient decreased. The dominant wear mechanism at 350℃ was delamination for QCs. The cracks formed on the worn surface during the friction. Moreover, phase transformation was not observed on worn surface of QCs at 350℃. All the results are discussed and explained.
参考文献
| [1] | SLChang;W B Chin;C M Zhang;C J Tenks and P A Thiel .[J].Surface Science Spectra,1995,337:135. |
| [2] | KongJUAN;Chungen ZHOU;Shengkai GONG;Huibin XU .[J].Surface and Coatings Technology,2003,165:281. |
| [3] | JMDuois.[A].World Scientific singapore,1997:208. |
| [4] | JMDuois;S S Kang;A Perrot .[J].Materials Science and Engineering,1994,179/180:122. |
| [5] | CJJenksandPAThiel .[J].Langmuir,1998,14:1392. |
| [6] | SSKang;J M Duois .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1992,66:151. |
| [7] | JVonSteut;J M Soro;P Plaindoux;J M Dubois.[M].New Horizons in Quasicrystals Research and Applications AmesIowa,1996 |
| [8] | SSKang;J M Dubois;J von Stebut.[J].Journal of Materials Research,1993(08):2471. |
| [9] | DJSordelet;M F Besser;M J L Logsdon .[J].Materials Science and Engineering,1998,255:54. |
| [10] | Chungen ZHOU,Huibin XU,Shengkai GONG,Guangming KANG.Formation and Oxidation Behavior of Al-Cu-Fe Quasicrystal[J].材料科学技术学报(英文版),2002(03):251-253. |
| [11] | 周细应,罗军明,万润根.温度对准晶材料摩擦性能的影响[J].摩擦学学报,2002(03):232-234. |
| [12] | Jstraffelini;M Santella .[J].Materials Science and Technology,1998,2(14):143. |
| [13] | Yertier;M Godet;M Brendle .[J].Tribology Transactions,1989,32(04):490. |
| [14] | JiasuSUN.[M].Wear of Metal Metallurgical Industrial Press Bei jing,1992:269. |
| [15] | XiyongFU .[J].Michael L Falk and D A Rigney Wear,2001,250:420. |
| [16] | JSKo;A J Gellman;T A Lograsso;C J Jenks and P A Thiel .[J].Surface Science Spectra,1999,423:243. |
| [17] | YDing;D O Northwood;A T Alpas .[J].Surface and Coatings Technology,1997,96:140. |
| [18] | Pierrerunet;L M Zhang;Daniel J Sordelet;Matt Besser and Jean-Marie Dubois .[J].Materials Science and Engineering,2000,294-296:74. |
| [19] | Y. Wang;M. Hadfield .A mechanism for nucleating secondary fractures near a pre-existing flaw subjected to contact loading[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(7/8):597-605. |
| [20] | E. Fleury;S. M. Lee;J. S. Kim;D. H. Kim;W. T. Kim;H. S. Ahn .Tribological properties of Al-Ni-Co-Si quasicrystalline coatings against Cr-coated cast iron disc[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2002(9/10):1057-1069. |
| [21] | VDemange;J W Anderegg;J Ghanbaja;F Machizaud D J Sordelet M Besser P A Thiel and J M Dubois .[J].Surface Science Applications,2001,173:327. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%