系统研究了自制羧基离子交换纤维对电镀废水中Ni 2＋的吸附性能。结果表明钠型羧酸纤维的平衡吸附容量远高于相应氢型纤维;静态条件下纤维对Ni 2＋的吸附容量可达220mg/g以上;溶液初始浓度、pH值以及温度越高,钠型羧酸纤维的平衡吸附量越大。100～300mg/L范围内的含镍电镀废水经柱吸附后可达国家规定排放浓度（≤0.5mg/L）,吸附Ni 2＋后的纤维可用2mol/L盐酸溶液解吸,纤维重复使用100次后吸附性能基本不变。
The adsorption performance ot carboxylicacid ion exchange ,was studied. The results showed that the adsorption capacity of sodium type carboxylic fiber was much higher than one of the free carboxylic fiber under the same conditions, and the adsorption capacity of sodium type fiber for Ni2＋ could be up to 220mg/g. The larger the initial concentration, pH value and temperature of containing nickel solution were, the adsorption capacity of the functional fiber was higher. The CN2＋ of filtrate was lower than 0.5mg/L in the column adsorption process when CNi2＋ were from 100 mg/ L to 300 mg/ L. The fiber adsorbed Ni2＋ could be desorbed by aq. HCl （2mol/ L） , and the adsorption performance of the fiber did not significantly decline after 100 adsorption-desorption cycles.
参考文献
| [1] | 肖先念,刘杰,黄少斌,周瑞兴,张勇.R502螯合树脂吸附硫酸根溶液中高含量镍离子研究[J].水处理技术,2011(04):45-48,71. |
| [2] | 袁彦超,章明秋,容敏智.交联壳聚糖树脂对Ni（Ⅱ）的吸附行为研究[J].化学学报,2005(18):1753-1758. |
| [3] | Popuri SR;Vijaya Y;Boddu VM;Abburi K .Adsorptive removal of copper and nickel ions from water using chitosan coated PVC beads[J].Bioresource Technology: Biomass, Bioenergy, Biowastes, Conversion Technologies, Biotransformations, Production Technologies,2009(1):194-199. |
| [4] | 谢建军,吴海刚,蒋佳星,屠国平.PAAS高吸水树脂对重金属离子盐溶液的吸液及吸附性能[J].功能材料,2007(08):1331-1333. |
| [5] | 张艳丽,李冬光,蒋登高.后交联纤维的制备及吸附性能研究[J].功能材料,2007(03):505-508. |
| [6] | 王金涛,原思国,赵林,王毅.羧酸型离子交换纤维的制备与性能[J].合成纤维工业,2001(06):13-17. |
| [7] | 王磊,李仲谨,赖小娟.淀粉微球对Co2+的吸附热力学和动力学研究[J].功能材料,2010(z2):339-342. |
| [8] | Chang H uaichun;Song Nannan;Sun Qingfeng.Adsorption properties of 8-hydroeyquinoline chelating resin based on phenolic resin skeleton[J].Journal of Functional Materials,2010(z1):108-112. |
| [9] | 王金涛,李保,梁志宏,赵林,原思国.羧酸型阳离子交换纤维对过渡金属离子的吸附性能研究[J].河南化工,2002(09):8-10. |
| [10] | Yan G;Viraraghavan T;Chen M .[J].Adsorption Science and Technology,2001,19(01):25-43. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%