EFFECTS OF DIFFERENT FUNCTIONAL GROUP-CONTAINING ORGANICS ON MORPHOLOGY-CONTROLLED SYNTHESIS OF SILVER NANOPARTICLES AT ROOM TEMPERATURE

金属学报(英文版), 2006, 19(5): 362-370.

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.Faculty of Chemistry and Chemical Engineering, Jiangsu University, Zhenjiang 212013, China

2.Faculty of Chemistry and Chemical Engineering, Jiangsu University, Zhenjiang 212013, China

3.Faculty of Chemistry and Chemical Engineering, Jiangsu University, Zhenjiang 212013, China

4.Faculty of Chemistry and Chemical Engineering, Jiangsu University, Zhenjiang 212013, China

5.Department of Chemical Engineering, Jiangsu Teachers University of Technology, Changzhou 213001,China

6.Faculty of Chemistry and Chemical Engineering, Jiangsu University, Zhenjiang 212013, China

基金项目: Jiangsu University Advanced Research Foundation(1281310001) The Research Foundation from Chinese Education Department(2003406)

EFFECTS OF DIFFERENT FUNCTIONAL GROUP-CONTAINING ORGANICS ON MORPHOLOGY-CONTROLLED SYNTHESIS OF SILVER NANOPARTICLES AT ROOM TEMPERATURE

Keywords： silver nanoparticle

Silver nanoparticles with average particles sizes ranging from 2 to 131nm were manipulatively synthesized starting from silver nitrate using different functional group-containing organic modifiers at room temperature. The effects of the organic modifiers on the morphology of the resulting silver nanoparticles were strongly dependent on the intrinsic properties of the functional groups and the reducibility of the reductant. Numerous ether bonds (-O-) present in polyethylene glycol and Tween-80 were beneficial to the formation of silver nanoparticles with particle sizes of several nanometers in a narrow size distribution in both weak and strong reducing environments.Cetyltrimethylammonium bromide induced the formation of nanosized silver triangle plates in a weak reducing environment. The crystal growth of the silver nanoparticles with particle sizes of more than 10nm was postulated through an adhesion process of small-sized particles followed by a subsequent coalescence process under the present reaction conditions.

参考文献

[1]	F. Bonet;S. Grugeon;R. Herrera Urbina .In situ deposition of silver and palladium nanoparticles prepared by the polyol process, and their performance as catalytic converters of automobile exhaust gases[J].Solid state sciences,2002(5):665-670.
[2]	M Brust;C J Kiely .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2002,202:175.
[3]	R Chapman;P Mulvaney .[J].Chemical Physics Letters,2001,349:358.
[4]	A. Heilmann;A. Kiesow;M. Gruner;U. Kreibig .Optical and electrical properties of embedded silver nanoparticles at low temperatures[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(0):175-178.
[5]	H S Shin;H C Choi;Y Jung;S.B.Kim, H.J.Song H.J.Shin .[J].Chemical Physics Letters,2004,383:418.
[6]	Y Tan;Y Wang;L Jiang;D.Zhu .[J].Journal of Colloid and Interface Science,2002,249:336.
[7]	Y Li;Y Wu;B S Ong .[J].Journal of the American Chemical Society,2005,127:3266.
[8]	L Zhang;J C Yu;H Y Yip;Q.Li, K.W.Kwong, A.W.Xu P.K.Wong .[J].Langmuir,2003,19:10372.
[9]	L P Jiang;A N Wang;Y Zhao;J.R.Zhang J.J.Zhu.[J].Inorganic Chemistry Communications,2004(07):506.
[10]	M K Temgire;S S Joshi .[J].Radiation Physics and Chemistry,2004,71:1039.
[11]	H S Shin;H J Yang;S B Kim;M.S.Lee .[J].Journal of Colloid and Interface Science,2004,274:89.
[12]	H Yin;T Yamamoto;Y Wada;S.Yanagida .[J].Materials Chemistry and Physics,2004,83:66.
[13]	Z Zhang;L Zhang;S Wang;W.Chen Y.Lei .[J].Polymer,2001,42:8315.
[14]	J Y Chang;J J Chang;B Lo;S.H.Tzing Y.C.Ling .[J].Chemical Physics Letters,2003,379:261.
[15]	A Kameo;T Yoshimura;K Esumi .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2003,215:181.
[16]	B Yin;H Ma;S Wang;S.Chen .[J].Journal of Physical Chemistry B,2003,107:8898.
[17]	K Abe;T Hanada;Y Yoshida;N.Tanigaki, H.Takiguchi, H.Nagasawa, M.Nakamoto, T.Yamaguchi K.Yase .[J].THIN SOLID FILMS,1998,327-329:524.
[18]	S N Abdullin;A L Stepanov;Y N Osin;I.B.Khaibullin .[J].Surface Science,1998,395:L242.
[19]	R Patakfalvi;A Oszko;I Dékány .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2003,220:45.
[20]	P.V. Adhyapak;P. Karandikar;K. Vijayamohanan .Synthesis of silver nanowires inside mesoporous MCM-41 host[J].Materials Letters,2004(7/8):1168-1171.
[21]	J H Park;Y G Kim;C Oh;S.I.Shin, Y.C.Kim, S.G.Oh S.H.Kong .[J].Materials Research Bulletin,2005,40:271.
[22]	V Hornebecq;M Antonietti;T Cardinal;M.Treguer-Delapierre .[J].Chemistry of Materials,2003,15:1993.
[23]	M Cai;J Chen;J Zhou .[J].Surface Science Applications,2004,26:422.
[24]	M.J.Rosemary;T.Pradeep .Solvothermal synthesis of silver nanoparticles form thiolates[J].Journal of Colloid and Interface Science,2003(1):81-84.
[25]	L Sun;Z Zhang;H Dang .[J].Materials Letters,2003,57:3874.
[26]	M P Pileni.[J].Supramolecular Science,1998(05):321.
[27]	Z Zhang;M Han .[J].Chemical Physics Letters,2003,374:91.
[28]	Y Tan;Y Li;D Zhu .[J].Journal of Colloid and Interface Science,2003,258:244.
[29]	S Kéki;J Torok;G Deák;L.Daroczi M.Zsuga .[J].Journal of Colloid and Interface Science,2000,229:550.
[30]	P Kuo;W Chen .[J].Journal of Physical Chemistry B,2003,107:11267.
[31]	J Liu;W Ong;A E Kaifer .[J].Langmuir,2002,18:5981.
[32]	X Li;J Zhang;W Xu;H.Jia, X.Wang, B.Yang, B.Zhao, B.Li Y.Ozaki .[J].Langmuir,2003,19:4285.
[33]	A B R Mayer;J E Mark .[J].Polymer,2000,41:1627.
[34]	P Raveendran;J Fu;S L Wallen .[J].Journal of the American Chemical Society,2003,125:13940.
[35]	M Lee;S Oh;K Suh;D.Kim D.Sohn .[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2002,210:49.
[36]	J Zhang;P Chen;C Sun;X.Hu .[J].Applied Catalysis A:General,2004,266:49.
[37]	H Huang;X Yang .[J].Carbohydrate Release,2004,339:2627.
[38]	B.L.V.Prasad;Sujatha K.Arumugam;Tanushree Bala;Murali Sastry .Solvent-Adaptable Silver Nanoparticles[J].Langmuir: The ACS Journal of Surfaces and Colloids,2005(3):822-826.
[39]	Y Sun;Y Yin;B T Mayers;T.Herricks Y.Xia .[J].Chemistry of Materials,2002,14:4736.
[40]	Y Sun;B Mayers;T Herricks;Y.Xia.[J].Nano Letters,2003(03):955.
[41]	D Yu;V W Yam .[J].Journal of Physical Chemistry B,2005,109:5497.
[42]	I Sondi;D V Gola;E Matijevi(c) .[J].Journal of Colloid and Interface Science,2003,260:75.
[43]	D D Evanoffand;G Chumanov .[J].Journal of Physical Chemistry B,2004,108:13948.
[44]	Z H Mbhele;M G Salemane;C G C E Van Sittert;J.M.Nedeljkovi(c), V.Djokovi(c) A.S.Luyt .[J].Chemistry of Materials,2003,15:5019.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

EFFECTS OF DIFFERENT FUNCTIONAL GROUP-CONTAINING ORGANICS ON MORPHOLOGY-CONTROLLED SYNTHESIS OF SILVER NANOPARTICLES AT ROOM TEMPERATURE

参考文献