对比了聚丙烯(PP)基体中,不同填料对聚磷酸铵(APP)-季戊四醇(PER)与磷酸胍(GP)-PER膨胀型阻燃(IFR)体系产生的不同影响,并以填料SiO2、CaCO3、SNO3以及Al2O3为代表,进行了研究.极限氧指数(LOI)结果表明填料与APP-PER体系复配后,LOI提高,并产生协同作用,但与GP-PER体系复配后,LOI降低,产生拮抗作用.SEM-EDS结果表明,填料加入APP-PER体系后改善了炭层致密性,炭层中的填料被大量可溶性含磷降解产物(PDPs)包覆、粘结,而填料加入GP-PER体系后却富集在炭层表面,破坏炭层致密性.X射线衍射结果表明,GP-PER体系的炭层表面富集的粒子为填料本身或相应磷酸盐以及聚磷酸盐.热失重、离子色谱等测试表明,在2种IFR体系产生的炭层中,PDPs的含量和性状差异较大,应是填料对炭层产生协同或拮抗作用的关键因素之一.
参考文献
| [1] | Na Li;Yin Xia;Zongwen Mao .Synergistic Effect of SiO2 on Intumescent Flame-retardant Polypropylene[J].Polymers & Polymer Composites,2013(7):439-447. |
| [2] | Serge Bourbigot;Michel Le Bras;Rene Delobel;Patrice Breant;Jean-Michel Tremillon .4A zeolite synergistic agent in new flame retardant intumescent formulations of polyethylenic polymers—study of the effect of the constituent monomers[J].Polymer Degradation and Stability,1996(2/3):275-287. |
| [3] | Ming Chian Yew;N.H. Ramli Sulong .Fire-resistive performance of intumescent flame-retardant coatings for steel[J].Materials & design,2012(Feb.):719-724. |
| [4] | De-Yi Wang;Yun Liu;Yu-Zhong Wang;C. Perdomo Artiles;T. Richard Hull;Dennis Price .Fire retardancy of a reactively extruded intumescent flame retardant polyethylene system enhanced by metal chelates[J].Polymer Degradation and Stability,2007(8):1592-1598. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%