采用低毒单体N,N-二甲基丙烯酰胺(DMAA)制备了氧化锆增韧氧化铝(ZrO2/Al2 O3,ZTA)陶瓷,氧化铝与氧化锆的质量比为3∶1,浆料的固相体积分数为50 vol％.讨论了不同干燥方式对干燥速率以及坯体性能的影响,研究了不同成型温度对坯体性能的影响.通过研究发现,在湿热烘箱中干燥的坯体强度最高,成型温度应控制在65℃附近.通过对不同单体含量的坯体烧结后陶瓷性能的对比,发现单体的加入量为10wt％左右较好,通过与干压成型陶瓷性能的对比,发现注凝成型得到的陶瓷强度和韧性分别提高了42.2％和23.5％,达到640 MPa和6.3MPa.m1/2,通过扫描电镜图片分析发现,注凝成型制得的陶瓷结构更均匀.
参考文献
| [1] | 郭瑞松,杨正方,袁启明,陈玉如,郭多力.复合助剂对ZTA陶瓷烧结性的影响[J].硅酸盐学报,1999(02):258. |
| [2] | Liu X L;Huang Y;Yang J L .Effect of Rheological Properties of the Suspension on the Mechanical Strength of Al2 O3-ZrO2 Composites Prepared by Gelcasring[J].Ceramics International,2002,2g:159-164. |
| [3] | Ometete O O;Janney M A;Strehlow R A .G elcasting-a New Ceramic Forming Process[J].Ceramic Bulletin,1991,70(10):1641-1648. |
| [4] | 刘炜;杨金龙;董英鸽 等.颗粒级配对凝胶注模成型氧化铝陶瓷的影响[J].人工晶体学报,2009,38:211-214. |
| [5] | Ma J T;Xie Z P;Miao H Z et al.Gelcasting of Alumina Ceramics in the Mixed Acrylamide and Polyacrylamide Systems[J].Journal of the European Ceramic Society,2003,23:2273-2279. |
| [6] | 仝建峰,陈大明.部分稳定氧化锆陶瓷的凝胶注模成型工艺[J].硅酸盐学报,2008(11):1620-1624. |
| [7] | 郭文利,徐廷献,燕青芝,葛昌纯.N-羟甲基丙烯酰胺聚合体系注凝成型纳米氮化硅陶瓷[J].硅酸盐学报,2006(02):147-151. |
| [8] | Ibram Ganesh;Susana M. Olhero;Paula M.C. Torres .Hydrolysis-induced aqueous gelcasting for near-net shape forming of ZTA ceramic composites[J].Journal of the European Ceramic Society,2009(8):1393-1401. |
| [9] | Shen LY;Liu MJ;Liu XZ;Deng L;Li B .Investigation of the influencing factors on surface exfoliation on Al2O3-ZrO2 green bodies prepared by gelcasting[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1-2):63-67. |
| [10] | Kookabi M;Babaluo A A;Barati A .Gelation Process in Low-toxic Gelcasting Systems[J].Journal of the European Ceramic Society,2006,26:3083-3090. |
| [11] | Santacruz I;Nieto M I;Moreno R .Alumina Bodies with Near-to-theoretical Density by Aqueous Gelcasting using Concentrated Agarose Solutions[J].Ceramics International,2005,31:439-445. |
| [12] | GregorováE;Pabst W;ZivcováZ.Porous Alumina Ceramics Prepared with Wheat Flour[J].Journal of the European Ceramic Society,2010:1-10. |
| [13] | J. Chandradass;Ki Hyeon Kim;Dong sik Bae .Starch consolidation of alumina: Fabrication and mechanical properties[J].Journal of the European Ceramic Society,2009(11):2219-2224. |
| [14] | H. Akhondi;E. Taheri-Nassaj;H. Sarpoolaky .Gelcasting of alumina nanopowders based on gelation of sodium alginate[J].CERAMICS INTERNATIONAL,2009(3):1033-1037. |
| [15] | H. Akhondi;E. Taheri-Nassaj;A. Taavoni-Gilan .Gelcasting of alumina-zirconia-yttria nanocomposites with Na-alginate system[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):452-457. |
| [16] | Cai K;Huang Y;Yong J L .Alumina Gelcusting by using HEMA System[J].Journal of the European Ceramic Society,2005,25:1089-1093. |
| [17] | Zhang T;Zhang ZQ;Zhang JX;Jiang DL;Lin QL .Preparation of SiC ceramics by aqueous gelcasting and pressureless sintering[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):257-261. |
| [18] | 王金锋,高雅春,谢志鹏,孙加林.聚乙二醇用于注凝成型ZrO2坯体干燥研究[J].人工晶体学报,2007(06):1339-1342. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%