Multilayered Pt/Ru modified aluminide coating for thermal barrier coating (TBC) systems has been investigated. 2 μm Pt+2 μm Ru+2 μm Pt was first deposited on nickel-base superalloy DZ125 by electrodeposition, and then the coating was treated by annealing and a conventional pack-cementation aluminizing process. The cyclic oxidation tests were carried out at 1423 K in air. It was found that the thermal cyclic oxidation resistance of Pt/Ru-modified aluminide coating was comparable to that of Pt-modified aluminide coating, which was much better than simply aluminized DZ125. The addition of Ru to Pt-modified aluminide coating increased the resistance to rumpling. The microstructures and phase constitutions of the coating before and after oxidation were investigated.
参考文献
| [1] | |
| [2] | |
| [3] | H.B. Xu and H.B. Guo: Surf. Coat. Technol., 2000, 130, 133.[2 ] W.J. Brindley and R.A. Miller: Surf. Coat. Technol., 1990, 43-44, 446.[3 ] A.G. Evans, D.R. Mumm, J.W. Hutchinson, G.H. Meier and F.S. Pettit: Prog. Mater. Sci., 2001, 46, 505.[4 ] C. Leyens, U. Schulz, B.A. Pint and I.G. Wright: Surf. Coat. Technol., 1999, 120, 68.[5 ] V.K. Tolpygo and D.R. Clarke: Acta Mater., 2000, 48(13), 3283.[6 ] V.K. Tolpygo and D.R. Clarke: Acta Mater., 2004, 52(17), 5115.[7 ] V.K. Tolpygo and D.R. Clarke: Acta Mater., 2004, 52(17), 5129.[8 ] D.R. Mumm , A.G. Evans and I.T. Spitsberg: Acta Mater., 2001, 49(12), 2329.[9 ] P.J. Hill, P. Ellis, L.A. Cornish, M.J. Witcomb and I.M. Wol® |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%