The mechanical behavior of 2124 Al alloy produced by powder metallurgy was investigated with compression test at different temperatures and strain rates. The tests were performed in the temperature range of 300℃～500℃ and at strain rates from 0.001 s-1 to 1.0 s-1. The compression flow curves exhibited an initial sharp increase with strain, followed by monotonous hardening. The maximum stress decreased with decreasing strain rate and increasing temperature. The hot deformation characteristics of the material were studied using processing maps. The domain of safety and unsafe regime were identified and validated through microstructural examination.
参考文献
| [1] | A Sato;R Mehrabian.[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1976(07):443. |
| [2] | C S Lee;Y H Kim;K S Han .[J].Journal of Materials Science,1992,27:793. |
| [3] | I Prigogine;I Stengers.Order Out of Chaos[M].Bantam Books,New York,1984 |
| [4] | P R Gibson;A J Clegg;A A Das .[J].Wear,1984,95:193. |
| [5] | F Weiss;H Froes;D Eylon;E Welsch .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17:1935. |
| [6] | J Jonas;C M Sellars;W J Mcg Tegart .[J].Metal Rev,1969,14(01) |
| [7] | Y V R K Prasad;H L Gegel;S M Doraivelu;J C Malas, J T Organ, K A Lark and D R Barker .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1984,15:1883. |
| [8] | Y V R K Prasad;S Sasidhara.Hot Working Guide:A Compendium of Processing Maps[M].ASM International,Materials Park,1997 |
| [9] | A K S Kalyan Kumar .[D].Indian Institute of Science,Bangalore,India,1987. |
| [10] | Ziegler;I N Snddon;R E Hill.Progress in Solid Mechanics[M].North-Holland,Amsterdam,1963:93. |
| [11] | H J Frost;M F Ashby.Deformation Mechanism Maps[M].Pergaman Press,London,1982 |
| [12] | R Raj.[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1981(12):1089. |
| [13] | P E Wellstead.Introduction to Physical System Modeling[M].New York:Academic Press,1979:144,9. |
| [14] | X X Xia;P Sakaris;H J Mcqueen .[J].Materials Science and Technology,1994,16:487. |
| [15] | S V Narayanamurthy;B Nageswararao;B P Kashyap .[J].International Materials Reviews,2000,45:15. |
| [16] | B V Radhakrishna Bhatt;Y R Mahajan;Y V R K Prasad .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31:629. |
| [17] | Manish D Dighe;Arun M Gokhale;Marc F Horstemeyer;D A Mosher .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000,31:1725. |
| [18] | C Gandhi .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1982,13:1233. |
| [19] | C M Styles;I Sinclair;P J Gregson;S M Flitcroft.[J].Materials Science and Technology,1994(10):475. |
| [20] | B L Zhang;M S Maclean;T N Baker .[J].Materials Science and Technology,2000,16:897. |
| [21] | Y. V. R. K. Prasad;T. Seshacharyulu;S. C. Medeiros;W. G. Frazier .Effect of preform microstructure on the hot working mechanisms in ELI grade Ti-6Al-4V: transformed β v. equiaxed (α+β)[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2000(5):511-516. |
| [22] | S Venugopal;S L Mannan.[A].Annamalai University,India,2003:30. |
| [23] | M J Luton;C M Sellars .[J].Acta Materialia,1969,17:1033. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%