Bulk Zr55Al10Ni5Cu30 metallic glass plates with a dimension of 85 mm×35mm×4 mm and a complicated plate werefabricated by injecting casting method using spongy zirconium and industrial purity aluminum, nickel and copper asraw materials. It was shown that the holding time of liquid metals at elevated temperatures had a great influence onthe oxygen content of the plates due to the contamination resulting from the atmosphere. Increasing holding timeresulted in the increase of oxygen content in the injected alloy. The glass transition temperatures of the bulk metallicglass plates are higher than that reported in the literature and crystallization temperature is lower for the one withhigher oxygen content at the same heating rate. The extension of the undercooled liquid region △Tx reaching about87 K is 3 K higher than that previously reported and 26 K higher than that with oxygen content of 0.076 wt pct forthe one with oxygen content as high as 0.065 wt pct. Therefore the oxygen content of the alloy has a significantinfluence on the glass forming ability and thermal stability of bulk metal glass. It is suggested that direct correlationbetween high glass forming ability and large △Tx is only valid for a well-defined Iow oxygen concentration or has tobe reconsidered by incorporating oxygen as an additional alloying element.
参考文献
| [1] | A.Inoue .Stabilization of metallic supercooled liquid and bulk amorphous alloys[J].Acta materialia,2000(1):279-306. |
| [2] | W L Johnson .[J].MRS Bulletin,1999,10:42. |
| [3] | A Inoue;T Zhang .[J].Materials Transactions,1996,37:185. |
| [4] | J.M.Barandiaran;J.Colmenero .[J].Journal of Non-Crystalline Solids,1981,46:277. |
| [5] | J. Eckert;N. Mattern;M. Zinkevitch. M. Seidel .Crystallization behavior and phase formation in Zr-Al-Cu-Ni metallic glass containing oxygen[J].Materials transactions,1998(6):623-632. |
| [6] | A Inoue;Y Kawamura;TShibata;K.Sasamori .[J].Materials Transactions,1996,37:1337. |
| [7] | T Zhang;A Inoue;NNishiyama;K Ohbaand T Masumoto .[J].Materials Transactions,1993,34:1234. |
| [8] | Y Li;J Mater .[J].Science Technology,1999,15:97. |
| [9] | H H Hng;Y Li;SCNg;C.K.Ong .[J].Journal of Non-Crystalline Solids,1996,208:127. |
| [10] | X H Lin;W L Johnson .[J].Journal of Applied Physics,1995,78:6514. |
| [11] | A. Gebert .Effect of oxygen on phase formation and thermal stability of slowly cooled Zr65Al7.5Cu17.5Ni10 metallic glass[J].Acta materialia,1998(15):5475-5482. |
| [12] | X. H. Lin;W. L. Johnson;W. K. Rhim .Effect of Oxygen Impurity on Crystallization of an Undercooled Bulk Glass Forming Zr-Ti-Cu-Ni-Al Alloy[J].Materials transactions,1997(5):473-477. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%