选用Q235和Q345钢,在纯锌浴和含钛量分别为0.05％、0.1O％、0.15％、0.20％(质量分数)的合金浴中浸镀0.5、1、3、5、8 min.利用扫描电子显微镜和能谱仪研究了钛对热浸镀锌组织和生长动力学的影响,并提出钛对含硅钢铁锌反应抑制作用的机理.结果表明:钛的加入缩短了Γ的孕育期,促进了合金层中δ的生长和ζ的消失,δ的生长依然受扩散控制,呈抛物线生长规律;Zn-0.05％ Ti锌浴可以很好的抑制高硅钢的硅反应性;含硅钢热浸镀锌钛合金浴时,在锌浴中会形成锌铁钛三元T相,该相能吸收ζ晶界处富集的硅,从而抑制了铁锌反应.
参考文献
| [1] | Sandlin R W .Galvanizing characteristics of different types of steel[J].Wire and Wire Products,1941,16:28-35. |
| [2] | Chidambaram P R;Rangarajan V;Van Ooij W J .Characterization of high temperature hot dip galvanized coatings[J].Surface and Coatings Technology,1991,46(03):245-253. |
| [3] | 车淳山 .Sandelin效应机理及其抑制方法研究[D].华南理工大学,2005. |
| [4] | Chen Z W;Kennon N F;See J B et al.Technigalva and other development in batch hot-dip galvanizing[J].JOM,1992,44(01):22-26. |
| [5] | Reumont G;Foct J;Perrot P.[A].Berlin:EGGA,2000 |
| [6] | 李发国,尹付成,苏旭平,李智.钴对含硅钢镀锌层的组织和生长动力学的影响[J].中国有色金属学报,2010(01):86-91. |
| [7] | Su, X.;Wu, C.;Liu, D.;Yin, F.;Zhu, Z.;Yang, S. .Effect of vanadium on galvanizing Si-containing steels[J].Surface & Coatings Technology,2010(1):213-218. |
| [8] | 吴长军,苏旭平,王建华,王鑫铭,涂浩.Zr，Co，Ni，V微合金化对含硅结构钢热浸镀锌性能的影响[J].材料热处理学报,2012(01):69-73. |
| [9] | Gloriant T;Reumont G;Perrot P .The Fe-Zn-Ti system at 450 ℃[J].ZEITSCHRIFT FUR METALLKUNDE,1997,88(07):539-544. |
| [10] | Pistofidis N;Vourlias G;Pavlidou E;Stergioudis G .Effect of Ti, Ni and Bi addition to the corrosion resistance of Zn hot-dip galvanized coatings[J].Journal of optoelectronics and advanced materials,2007(6):1653-1659. |
| [11] | Gueorgui P. Vassilev .Contribution to the zinc-rich side of the Ti-Zn system[J].Zeitschrift fur Metallkunde,2004(9):813-817. |
| [12] | G. P. Vassilev;X. J. Liu;K. Ishida .Reaction kinetics and phase diagram studies in the Ti-Zn system[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):162-170. |
| [13] | Tang Xian-hui;Yin Fu-cheng;Wang Xin-ming et al.The 450 ℃ isothermal section of the Zn-Fe-Ti system[J].Journal of Phase Equilibria and Diffusion,2007,28(04):355-361. |
| [14] | 李智,苏旭平,贺跃辉,谭铮,尹付成.Zn/Fe及Zn/Fe-Si固态扩散偶中金属间化合物的生长[J].中国有色金属学报,2008(09):1639-1644. |
| [15] | Jordan CE.;Marder AR. .FE-ZN PHASE FORMATION IN INTERSTITIAL-FREE STEELS HOT-DIP GALVANIZED AT 450 DEGREES-C .1. 0.00 WT-PERCENT AL-ZN BATHS[J].Journal of Materials Science,1997(21):5593-5602. |
| [16] | Kozdras M S;Niessen P .Silicon-induced destabilization of galvanized coating in the sandelin peak region[J].Metallograghy,1989,22(03):253-267. |
| [17] | Bretez M;Douphin J Y;Foct J et al.Phase relationships and diffusion paths in the system zinc vapour-iron silicon alloys at 773 and 973 K[J].ZEITSCHRIFT FUR METALLKUNDE,1987,78(02):137-140. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%