利用冷压-烧结技术制备了BaO掺杂的1ONiO-NiFe2O4复合陶瓷,研究了BaO掺杂量对1ONiO-NiFe2O4复合陶瓷物相组成及电导率的影响.结果表明,当BaO掺杂量为O～4%(质量分数)时,烧结样品中主要含有NiO和NiFe2O4两种,BaO促进了致密化烧结,降低了烧结温度;TG-DSC分析发现,在303～1233K温度范围内,1ONiO-NiFe2O4陶瓷在空气气氛中先吸氧后失氧;导电率测试表明,掺杂BaO能显著提高材料的高温电导率,且掺杂0.5%样品在1233K时材料达到最大电导率11.76S/cm,是未掺杂样品的12.8倍.
参考文献
| [1] | Pawlek R P.Inert Anodes:an Update[M].USA:TMS Warreudale PA,2002:449-456. |
| [2] | Weyand J D;DeYoung D H;Ray S P et al.Inert Anodes for Aluminium Smelting[R].Washington D C:Aluminum Company of America,February,1986. |
| [3] | Pawlek R P.Inert Anodes for The Primary Aluminum In-dustry:an Update[M].USA TMS Warreudale PA,1996:243-248. |
| [4] | LI Jie;LAI Yan-qing;ZHOU Ke-chao;LI Zhi-you;LIU Ye-xiang .Preparation and preliminary testing of cermet inert anode for aluminum electrolysis[J].Transactions of Nonferrous Metals Society of China,2003(3):663-670. |
| [5] | Keniry J .[J].Journal of the Minerals,Metals & Materials Society,2001,53(05):43-47. |
| [6] | Sadoway D R .[J].Journal of the Minerals,Metals & Materials Society,2001,53(05):34-35. |
| [7] | 席锦会,姚广春,刘宜汉,张晓明.五氧化二钒对铁酸镍基金属陶瓷惰性阳极导电行为的影响[J].硅酸盐学报,2006(01):34-38. |
| [8] | 田忠良,赖延清,段华南,孙小刚,张刚.掺杂SnO2对NiFe2O4陶瓷电导率的影响[J].矿产保护与利用,2004(05):37-40. |
| [9] | 张剑红,刘宜汉,席锦会,姚广春.掺杂TiO2的镍铁尖晶石的高温导电性[J].材料与冶金学报,2003(04):271-273. |
| [10] | 赖延清,张勇,张刚,李劼,贺跃辉,黄伯云,刘业翔.CaO掺杂对10NiO-NiFe2O4复合陶瓷烧结致密化的影响[J].中国有色金属学报,2006(08):1355-1360. |
| [11] | 赖延清,张刚,李劼,刘业翔.金属含量对Cu-Ni-NiFe2O4金属陶瓷导电性能的影响[J].中南大学学报（自然科学版）,2004(06):880-884. |
| [12] | 张雷,周科朝,李志友,张晓泳.气氛对NiFe2O4陶瓷烧结致密化的影响[J].中国有色金属学报,2004(06):1002-1006. |
| [13] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1997:265-331. |
| [14] | Weyand J D;DeYoung D H;Ray S P et al.Inert Anodes for Aluminium Smelting(Final Report)[R].Washington D C:Aluminum Company of America,February,1986. |
| [15] | Weyand J D.Manufacturing Processes Used for the Pro-duction of Inert Anodcs[M].USA:TMS,Warrendale,Pa,1986:32l-339. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%