本文提供了一种简单的热退火方法以制备线状TiO2纳米结构.热退火方法一直难以用于高熔点金属氧化物纳米结构的制备,而本文通过引入CuCl2作为催化剂,通过简单的反应过程,在较短的时间内和远低于钛熔点的反应温度下制得了金红石相的TiO2一维纳米结构.研究结果表明,关键的实验参数包括活性催化物添加量、生长温度和退火时间.在850℃(接近于Cu-Ti共晶温度)退火60分钟的反应条件下,制备的二氧化钛纳米线长度在10微米以上,直径约为100纳米.此外,本文还探讨了TiO2纳米线生长机理.
参考文献
| [1] | Francioso L;Siciliano P .Top-down contact lithography fabrication of a TiO2 nanowire array over a SiO2 mesa[J].Nanotechnology,2006(15):3761-3767. |
| [2] | Chen XB;Mao SS .Synthesis of titanium dioxide (TiO2) nanomaterials[J].Journal of nanoscience and nanotechnology,2006(4):906-925. |
| [3] | Xiang B;Zhang Y;Wang Z;Luo XH;Zhu YW;Zhang HZ;Yu DP .Field-emission properties of TiO2 nanowire arrays[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2005(8):1152-1155. |
| [4] | Li AP.;Birner A.;Nielsch K.;Gosele U.;Muller F. .Fabrication and microstructuring of hexagonally ordered two-dimensional nanopore arrays in anodic alumina[J].Advanced Materials,1999(6):483-487. |
| [5] | Masuda H;Yamada H;Satoh M;Asoh H;Nakao M;Tamamura T .Highly ordered nanochannel-array architecture in anodic alumina[J].Applied physics letters,1997(19):2770-2772. |
| [6] | Fu YY.;Wang RM.;Xu J.;Chen J.;Yan Y.;Narlikar A.;Zhang H. .Synthesis of large arrays of aligned alpha-Fe2O3 nanowires[J].Chemical Physics Letters,2003(3-4):373-379. |
| [7] | 袁志好,张立德.掺锌的TiO2纳米粉的结构相变及发光性质[J].高等学校化学学报,1999(07):1007-1011. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%