本文以NiO和Fe2O3为主要原料,采用机械化合-两步烧结法制备NiFe2O4基金属陶瓷试样.研究了球磨时间、助磨剂含量、球磨转速对制备前驱体粒度的影响,并利用X射线衍射和扫描电子显微镜等进行表征.结果表明,球磨参数越好,粉体颗粒越细,提高冷等静压压坯的致密度、降低试样烧结温度,最终提高惰性阳极试样密度,改善试样的导电性和抗腐蚀性等性能并达到保护环境、节约能源的效果.本实验制备惰性阳极球磨阶段最佳球磨条件为:助磨剂含量150 ml、球磨时间6h、球磨转速300 r/min,此条件下制得了体积密度为5.68 g/ml的阳极试样.
参考文献
| [1] | 丁海洋,卢世刚,阚素荣,张向军,杨娟玉.铝电解用金属惰性阳极的研究进展[J].稀有金属,2009(03):420-425. |
| [2] | 刘业翔.铝电解惰性阳极与可湿润性阴极的研究与开发进展[J].轻金属,2001(05):26-29. |
| [3] | Olsene,Thonstan J.The behaviour of nickel ferrite cermet ma terials as inert anodes[A].Warrendale PA:TMS,1996:249-257. |
| [4] | 于先进.铝冶金进展[M].沈阳:东北大学出版社,2001:431-434. |
| [5] | 陈喜平,刘凤琴.铝电解惰性阳极的研究现状[J].有色金属(冶炼部分),2002(04):23-26. |
| [6] | Kvande H.Inert electrodes in aluminum electrolysiscells[A].San Diego:The Minerals,Metals and Materials Society,1999:369-376. |
| [7] | 赖延清,黄蔚,田忠良,李新征.铝电解NiFe2O4基金属陶瓷惰性阳极性能研究进展[J].矿产保护与利用,2006(04):47-50. |
| [8] | 罗涛,王兆文,于旭光,高炳亮,石忠宁,邱竹贤.铝电解陶瓷类惰性阳极材料的发展[J].有色矿冶,2004(03):46-49. |
| [9] | Deyoung D H.Solubilities of oxides for inert anodes in cryolitebased melts[A].Warrendale,PA:The Minerals,Metals and Materials Society,1986:299-307. |
| [10] | Brindle R;Margolis N .Strategy for technology innovation in the US.aluminum industry[R].US:US Department of Ener gy,1999. |
| [11] | Li J;Zhang Q S;Lai Y Q .Thermal stresses relaxation design of Ni/ NiFe2O4graded cermet inert anode[J].Act Metallurical Sinica,2005,18:635-641. |
| [12] | Ray S P;Liu Xinghua;Weirauch D A et al.Inert anode containing oxides of nickel iron and cobalt useful for the electrolytic production of metals[P].US Patent,6372119,2002-04-16. |
| [13] | Yang J H;John N;Hyrn N.Aluminum electrolysis tests with inert anode in KF-AlF3-based electrolysis[A].,2008 |
| [14] | Shi Zhongning;Zhao Xingliang;Xu Junli.Anti-oxidation properties of iron-nickel alloys at 800～900℃[J].Light Metals,2008 |
| [15] | 何汉兵,黄伯云,李志友,周科朝.BaO掺杂对10NiO-NiFe2O4复合陶瓷烧结致密化的影响[J].中国有色金属学报,2008(05):851-855. |
| [16] | 张淑婷,姚广春,刘宜汉,席锦会.Ag-NiFe2O4金属陶瓷性能研究[J].材料科学与工艺,2007(01):111-114. |
| [17] | 任向东;同继锋 .氧化铝研磨介质的磨耗分析[J].全国性建材科技期刊-陶瓷,1991,1:8. |
| [18] | Criado J M;Gonzalez M;Real C.Correlation between crystallite size and micrstrains in materials subjected to tehermal and/or mechanical treatments[J].Journal of Materials Science Letters,1986(05):467-469. |
| [19] | 杨华明 .搅拌磨超细粉碎及机械化学的研究[D].中南工业大学,1998. |
| [20] | 赵旭光.助磨剂的助磨作用对粉体流变性能的影响[J].耐火材料,1999(05):147-149. |
| [21] | 张磊,焦万丽,姚广春.NiFe2O4惰性阳极的制备及其电解腐蚀机理[J].硅酸盐学报,2005(12):1431-1436. |
| [22] | 钱旭坤,朱春城,赫晓东.Co-Ni-xNiFe2O4惰性阳极的电导率及耐腐蚀性能[J].稀有金属材料与工程,2007(11):1979-1982. |
| [23] | 张丽鹏,于先进,董云会,李德刚.MnO2掺杂金属陶瓷惰性阳极的制备及性能研究[J].高等学校化学学报,2008(01):154-158. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%