为了提高钛合金的表面生物活性,采用在含有钙磷的电解液中对钛合金进行了微弧氧化,得到了含有钙磷的氧化层.研究了微弧氧化溶液浓度和氧化时间对膜层孔洞的影响,讨论了氧化膜中孔洞的形成和氧化膜生长机制.结果表明,在一定的条件下,电解液浓度的升高使得微弧氧化过程中电流密度相对增大,从而使得膜层孔洞增大.随着微弧氧化处理时间的延长,膜层表面的孔洞逐渐变小,最终封闭；膜层内钙含量随微弧氧化处理时间的延长而逐渐增多；膜层内磷含量先是增加,后有下降趋势.
参考文献
| [1] | 孙敬,崔振铎,朱胜利,杨贤金.生物医用植入钛及钛合金的力学性能研究及进展[J].金属热处理,2005(09):59-62. |
| [2] | 王永钱,江旭东,潘春旭.微弧氧化法原位生长TiO_2光催化薄膜及其复合技术[J].金属热处理,2010(03):20-25. |
| [3] | PENG Ji-hua,LI Wen-fang,HAN Bing,HUANG Fang-liang,DU Jun.Synthesis of tetragonal BaTiO3 film on Ti substrate by micro-arc oxidation[J].中国有色金属学会会刊（英文版）,2008(05):1117-1121. |
| [4] | Dong Q;Chen CZ;Wang DG;Ji QM .Research status about surface modification of biomedical Ti and its alloys by micro-arc oxidation[J].Surface review and letters,2006(1):35-43. |
| [5] | 刘荣明,郭锋,李鹏飞.电压对铝合金微弧氧化陶瓷层形成的影响[J].材料热处理学报,2008(01):137-140. |
| [6] | 薛文斌,邓志威,陈如意,张通和.钛合金在硅酸盐溶液中微弧氧化陶瓷膜的组织结构[J].金属热处理,2000(02):5-7. |
| [7] | Wang CX;Zhang D;Jiang YF .Growth process and wear resistance for ceramic coatings formed on Al-Cu-Mg alloy by micro-arc oxidation[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(2):674-678. |
| [8] | 徐可为.微弧氧化生成含钙磷氧化钛生物薄膜的结构[J].无机材料学报,2001(05):951-956. |
| [9] | Zhao, ZW;Chen, XY;Chen, AL;Huo, GS;Li, HG .Preparation of K2Ti6O13/TiO2 bio-ceramic on titanium substrate by micro-arc oxidation[J].Journal of Materials Science,2009(23):6310-6316. |
| [10] | Li LH;Kong YM;Kim HW;Kim YW;Kim HE;Heo SJ;Koak JY .Improved biological performance of Ti implants due to surface modification by micro-arc oxidation.[J].Biomaterials,2004(14):2867-2875. |
| [11] | Song WH.;Jun YK.;Han Y.;Hong SH. .Biomimetic apatite coatings on micro-arc oxidized titania[J].Biomaterials,2004(17):3341-3349. |
| [12] | Fu Liu;Ying Song;Fuping Wang;Tadao Shimizu;Kaoru Igarashi;Liancheng Zhao .Formation Characterization of Hydroxyapatite on Titanium by Microarc Oxidation and Hydrothermal Treatment[J].Journal of Bioscience and Bioengineering,2005(1):100-104. |
| [13] | 史兴岭,玄加申,位莉,王庆良.钛合金微弧氧化生物活性陶瓷膜润湿性及耐腐蚀性能研究[J].金属热处理,2008(07):37-41. |
| [14] | 付涛,憨勇,黄平,徐可为.微弧氧化-水热合成生物活性二氧化钛层的结构与性能[J].稀有金属材料与工程,2002(02):115-117. |
| [15] | 李夕金,程国安,薛文斌,郑瑞廷,吴晓玲,程云君.TiAl合金微弧氧化膜的制备及抗氧化性能研究[J].材料热处理学报,2006(05):95-99. |
| [16] | 蒋永锋,李均明,蒋百灵,符长璞.铝合金微弧氧化陶瓷层形成因素的分析[J].表面技术,2001(02):37-39. |
| [17] | 梁戈,赵仁兵,蒋百灵.电解液参数对铝合金微弧氧化黑色陶瓷膜性能的影响[J].材料热处理学报,2006(05):91-94. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%