研究了非晶合金Fe77.2Mo0.8Si9B13球磨过程中的晶化行为.结果表明:机械驱动的晶化产物为纳米尺寸单相α-Fe固溶体,与热晶化产物(α-Fe和3种硼化物)明显不同.
By using X-ray diffraction and transmission electron microscopy techniques, the crystallization process of an amorphous Fe77.2Mo0.8Si9B13 alloy during ball milling was investigated. It was found that the mechanically driven crystallization product is a na