采用断面形态特征与纤维对应拉伸曲线组合的对比分析方法,讨论了纤维的结构弱节及拉伸行为.结果表明,涤纶纤维的弱节主要是表层缺陷及其扩展所引起的,其力学性能为低应力、低应变、低断裂功特征.
参考文献
| [1] | Peirce F T .[J].Journal of Text Inst Transaction,1926,17:355-368. |
| [2] | 于伟东.纤维弱节的力学特征与判定[J].东华大学学报(自然科学版),2003(02):32-36. |
| [3] | Duckett K E;Krowicki R S;Cheng C C .[J].Applied Polymer Symposium,1975,27:359-368. |
| [4] | Hearle J W S;Lomas B;Cooke W D.in Atlas of Fibre Fracture and Damage to Textiles[M].CRC Press,UK,1998:57-67. |
| [5] | Ruetsch S B;Weigmann H D.Proc. 9th Intern. Wool Text. Res. Conf[C].,1995:44-56. |
| [6] | Yoshihara N;Ishihara H .[J].Journal of Textile Enginecring,2002,48(02):64-70. |
| [7] | Yu W;Postle R;Yan H .[J].Textile Asia,2001,32(11):38-42. |
| [8] | Sidorov O V;Shablygin M V;Gupper A et al.[J].Fibre Chemistry,2001,33(05):408-411. |
| [9] | Davis H;Singletary J;Srinivasarao M et al.[J].Textile Research Journal,2000,70(11):945-951. |
| [10] | Carr C M;Holt L A;Drennan J .[J].Textile Research Journal,1986,56(11):669-673. |
| [11] | 于伟东.纤维典型拉伸曲线及指标计算中的基本问题[J].西安工程科技学院学报,2003(03):229-235. |
| [12] | Cudet C;Bunsell A R;Hagege R et al.[J].Journal of Applied Polymer Science,29(12):4363-4376. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%