采用ECAP方法对TWIP钢(30Mn-3Si-3A1)试样进行一道次等径角挤压(ECAP)变形,对比研究原始态、一道次挤压态、ECAPlP+850℃×1h(空冷)处理和ECAPlP+1000℃×1h空冷处理后的微观结构及力学性能.试验结果表明:在变形过程中,形变孪晶的相互形变阻力和位错在形变孪晶界的大量塞积,使TWIP钢表现出很高的加工硬化率.试样经ECAPlP+1000℃×1 h空冷处理,与原始态相比在强度不变的情况下塑性有一定提高.同时,退火后晶粒的长大增加了位错沿孪晶界方向的剪切通道长度,增强了位错储存能力,从而表现出更高的塑性和加工硬化能力.试样经ECAPlP+850℃×1 h空冷处理后晶粒尺寸较小,增加了阻碍位错运动的有效界面,从而同样表现出很高的加工硬化能力.

参考文献

[1] Ruslan Z. Valiev;Terence G. Langdon .Principles of equal-channel angular pressing as a processing tool for grain refinement[J].Progress in materials science,2006(7):881-981.
[2] Huang CX;Gao YL;Yang G;Wu SD;Li GY;Li SX .Bulk nanocrystalline stainless steel fabricated by equal channel angular pressing[J].Journal of Materials Research,2006(7):1687-1692.
[3] 杨钢 等.径角挤压变形奥氏体不锈钢的结构演变和力学性能及应用研究[D].北京:钢铁研究总院,2007.
[4] 雍歧龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006:11.
[5] Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409.
[6] Iwahashi Y N;Wang J T;Horita Z J et al.Principle of Equal Channel Angular Pressing for the Processing of UltrafineGrained Materias[J].Scripta Materialia,1996,13:143.
[7] N. Q. Chinh;G. Horvath;Z. Horita .A new constitutive relationship for the homogeneous deformation of metals over a wide range of strain[J].Acta materialia,2004(12):3555-3563.
[8] 黄崇湘,吴世丁,李广义,刘腾,姜传斌,李守新.循环形变对超细晶铜室温拉伸行为的影响[J].金属学报,2004(11):1165-1169.
[9] 潘金生;仝健民;田民波.材料科学基础[M].北京:清华大学出版社,1998
[10] Kocks U F;Mecking H .Physics and Phenomenology of Strain Hardening:the FCC Case[J].Progress in Materials Science,2003,48:171.
[11] William D;Callister J.Fundamentals of Materials Science and Engineering[M].New York; John Wiley and Sons Inc,2001:64.
[12] Christian J W;Mahajan S .Deformation Twinning[J].Progress in Materials Science,1995,39:1.
[13] Kocks U F .Laws for Work-Hardening and Low-Temperature Creep[J].Journal of Eng Tech Trans ASME,1976,98:76.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%