以分析纯Bi2O3和Er2O3为原料,采用反向滴定共沉淀法合成Bi和Er的氢氧化物前驱体,并对共沉淀的pH值条件进行了分析.将该前驱体在500℃焙烧3h后得到Bi0.75Er0.25O1.5的纳米粉体,高温XRD结果表明该粉体主要为β相,谢乐公式计算平均晶粒尺寸为10nm,并且随温度升高在650℃转变为δ相.通过热力学计算,确定了SPS下烧结Bi0.75Er0.25O1.5陶瓷适宜的温度和氧分压条件,最后在测试温度为500℃保温1min得到了相对密度达到96%的δ相纳米晶的Bi0.75Er0.25O1.5陶瓷,平均晶粒尺寸为18nm.
参考文献
| [1] | Battle P D;Catlow C R A;Moroney L M .[J].Solid-State Chemistry,1987,67:42-50. |
| [2] | Fung K;Virkar A .[J].Journal of the American Ceramic Society,1991,74(08):1970-1980. |
| [3] | Jurado J R;Moure C;Duran P et al.[J].Solid State Ionics,1988,28-30:518-523. |
| [4] | Nakayama S .[J].Ceramics International,2002,28:907-910. |
| [5] | Zhen Q;Kale G M;Shi G .[J].Solid State Ionics,2005,176:2727-2733. |
| [6] | Wang Y Y;Peng W J;Chai L Y .[J].J Cent Southuniv Technol,2004,11(04):410-413. |
| [7] | 何伟明,甄强,潘庆谊,刘建强.反向滴定法制备超细氧化铋粉体的研究[J].功能材料,2003(06):702-703,706. |
| [8] | Stephen H;Stephen T.Solubilities of Inorganic Equilibria in Aqueous Solutions[M].Oxford:Pergamon Press,1963:1. |
| [9] | Wada S;Suganuma M;Kitagawa Y et al.[J].Journal of the Ceramic Society of Japan,1999,107(10):887-890. |
| [10] | 高濂;宫本大树 .[J].无机材料学报,1997,12(02):129-133. |
| [11] | Ye F;Liu J M;Zhang J X et al.[J].Composites Science and Technology,2008,68:1073-1079. |
| [12] | Luan W L;Gao L;Kawaoka H et al.[J].Ceramics International,2004,30:405-410. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%