以钒钛合金为原料,应用阳极氧化法制备出高度致密、有序的V掺杂TiO2纳米管阵列。应用扫描电镜（SEM）和粉末X光衍射仪（XRD）表征分析纳米管阵列的形貌和结构,结果表明在浓度不同的HF电解液下制备出径向不同的纳米管阵列,电解液浓度（0.5%～1.5%（质量分数））,管径变化（39.7～72.7nm）。在室温、可见光照射条件下,以10mg/L的亚甲基蓝溶液为模拟污染物进行光催化降解试验,研究了其光催化性能。结果显示V掺杂TiO2纳米管阵列光催化性能优于纯TiO2纳米管,且在HF电解液浓度为1.0%（质量分数）时制备出来的TiO2纳米管光催化降解有机毒物性能最佳。
The titanium vanadium alloy as raw material,using anode oxidation method,the highly dense,ordered vanadium doped titania nanotube arrays were fabricated.The nanotube arrays characterization of morphology,composition and structure were determined by scanning electron microscope（SEM）,energy disperse spectroscopy（EDS） and powder X-ray diffraction（XRD）,the results showed that the different weight concentrations of HF electrolyte prepared by radial different nanotube arrays,with the weight concentration of the electrolyte HF changing from（0.5% to 1.5wt%）,the variation of nanotube arrays＇ diameters was from 39.7 to 72.7nm.At room temperature,under visible light irradiation,photocatalytic degradation of 10mg/L methyleneblue solution was carried out to test its photocatalytic properties.The results showed vanadium doped titania nanotube arrays photocatalytic properties of titania nanotube arrays is better than that of pure sample S1,and the samples were fabricated under HF electrolyte weight concentration 1.0wt% have more photocatalytic efficiency than other experimental conditions.The mechanism was briefly discussed.
参考文献
| [1] | Gong D;Grimes C A;Varghese 0 K et al.Titanium oxide nanotube arrays prepared by anodic oxidation[J].Journal of Materials Research,2001,16:3331-3334. |
| [2] | Chu S Z;Lnoue S;Wada K et al.Highly porous(TiO^2-SiO^2-TeO^2 )/AlO^2/TiO^2 composite nanostructures on glass with enhanced photocatalysis fabricated by anodiza-tion and sol-gel process[J].Journal of Physical Chemistry B,2003,107:6586-6589. |
| [3] | Maggie Paulose;Oomman K Varghese;Gopal K Mor .Unprecedented ultra-high hydrogen gas sensitivity In undoped titania nanotubes[J].Nanotechnology,2006(2):398-402. |
| [4] | Yibing Xie;Li Min Zhou;Haitao Huang .Enhanced photoelectrochemical current response of titania nanotube array[J].Materials Letters,2006(29/30):3558-3560. |
| [5] | Susanta K.Mohapatra;Mano Misra;Vishal K.Mahajan .Design of a Highly Efficient Photoelectrolytic Cell for Hydrogen Generation by Water Splitting:Application of TiO_(2-x)C_x Nanotubes as a Photoanode and Pt/TiO2 Nanotubes as a Cathode[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2007(24):8677-8685. |
| [6] | Sun, WT;Yu, Y;Pan, HY;Gao, XF;Chen, Q;Peng, LM .CdS quantum dots sensitized TiO2 nanotube-array photoelectrodes[J].Journal of the American Chemical Society,2008(4):1124-1125. |
| [7] | Mor GK;Shankar K;Paulose M;Varghese OK;Grimes CA .Use of highly-ordered TiO2 nanotube arrays in dye-sensitized solar cells[J].Nano letters,2006(2):215-218. |
| [8] | Paulose M;Shankar K;Varghese O K et al.Backside illuminated dye-sensitized solar cells based on titania nanotube array eleetrodes[J].Nanotechnology,2006,17:1446-1448. |
| [9] | Popat K C;Eltgroth M;LaTempa T J et al.Titania nanotubes:a novel platform for drug-eluting coatings for medical implants[J].Small,2007,3:1878-1881. |
| [10] | Popat KC;Eltgroth M;Latempa TJ;Grimes CA;Desai TA .Decreased Staphylococcus epidermis adhesion and increased osteoblast functionality on antibiotic-loaded titania nanotubes.[J].Biomaterials,2007(32):4880-4888. |
| [11] | Roy SC;Paulose M;Grimes CA .The effect of TiO(2) nanotubes in the enhancement of blood clotting for the control of hemorrhage.[J].Biomaterials,2007(31):4667-4672. |
| [12] | Jong Hyeok Park;Sungwook Kim;Allen J.Bard .Novel Carbon-Doped TiO_2 Nanotube Arrays with High Aspect Ratios for Efficient Solar Water Splitting[J].Nano letters,2006(1):24-28. |
| [13] | T. Yamaki;T. Umebayashi;T. Sumita;S. Yamamoto;M. Maekawa;A. Kawasuso;H. Itoh .Fluorine-doping in titanium dioxide by ion implantation technique[J].Nuclear Instruments and Methods in Physics Research, Section B. Beam Interactions with Materials and Atoms,2003(0):254-258. |
| [14] | Shankar K;Tep KC;Mor GK;Grimes CA .An electrochemical strategy to incorporate nitrogen in nanostructured TiO2 thin films: modification of bandgap and photoelectrochemical properties[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2006(11):2361-2366. |
| [15] | Grimes DM;Grimes CA .A unique electromagnetic photon field using Feynman's electron characteristics and Maxwell's equations[J].Journal of computational and theoretical nanoscience,2006(5):649-663. |
| [16] | Sambrano JR;Nobrega GF;Taft CA;Andres J;Beltran A .A theoretical analysis of the TiO2/Sn doped (110) surface properties[J].Surface Science: A Journal Devoted to the Physics and Chemistry of Interfaces,2005(1/3):71-79. |
| [17] | 陈喜明,蒋新.掺杂钒对TiO2薄膜光诱导超亲水性的影响[J].浙江大学学报（工学版）,2006(01):145-148. |
| [18] | 陆同庆,王祥荣,杨其根.印染厂工业废水脱色净化处理及回用性研究[J].印染助剂,2005(08):31-32,35. |
| [19] | 王勇,张艳,赵亚伟,朱旭辉,徐宝龙.锰掺杂TiO2的制备、表征及光催化性能研究[J].染料与染色,2010(03):50-52,56. |
| [20] | 吴树新,马智,秦永宁,贾立山,黎洪瑞.过渡金属掺杂二氧化钛光催化性能的研究[J].感光科学与光化学,2005(02):94-101. |
| [21] | 马琦,张保柱,张志强,任建国,张智敏.水热法制备纳米Mn（Ⅱ）/TiO2粉体及其日光催化活性的研究[J].石油化工,2005(04):384-387. |
| [22] | La Y K;Sun N;Zhou J et al.Characteristic of TiO^2 nanotube array and photocatalytic performance[J].Journal of Functional Materials,2004,35:1958-1963. |
| [23] | 侯兴刚,吴晓玲,刘安东.Ag/TiO2薄膜光催化性能的研究[J].北京师范大学学报（自然科学版）,2005(06):604-607. |
| [24] | Wang Z Y;Tang P S;Jiang Y L et al.Study on fluorescence and diffuse reflection spectrum ot nanosized ToO^2[J].Rare Metal Mater & Engi,2004,33(zl):162-165. |
| [25] | Bms L .Electronic wave functions in semiconductor clusters:experiment and theory[J].Journal of Physical Chemistry,1986,90(12):2555-2560. |
| [26] | Hao E;Li S;Bailey R C et al.Optical properties of metal nano-shells[J].Journal of Physical Chemistry B,2004,108(04):1224-1228. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%