采用层压法制备了四种聚酯纤维布增强环氧树脂基复合材料,研究了不同填充物(纳米Al_2O_3颗粒和PTFE)对不同织物取向复合材料拉伸性能和摩擦磨损性能的影响,分析了拉伸断口和摩损表面的形貌.结果表明:加入PTFE使复合材料的经向和纬向的拉伸强度和弹性模量分别提高了1.4%,11.2%和31.5%,22.1%,纳米Al_2O_3颗粒的加入使复合材料的经向和纬向的拉伸强度和弹性模量分别提高了4.2%,14.2%和34.9%,26.3%;PTFE和纳米Al_2O_3均能提高复合材料的耐磨损性能,PTFE的加入使复合材料的摩擦因数降低了22.5%、磨损率减少了78.1%,Al_2O_3的加入使复合材料的摩擦因数增加了21.3%、磨损率减少了94.1%.
Four fiber reinforced epoxy resin composites were prepared by laminating method. The influence of different fillers of nano-particles and PTFE on the tensile and tribological properties of the composites with different fabric orientations was studied. The micrographs of tensile fracture and friction surfaces of the composites were also analyzed. The retuhs show that the tensile strength and modulus in warp and weft directions of the composites with the addition of PTFE increased 1.4%, 11. 2% and 31.5%, 22.1% respectively. While the same properties increased 4.2%, 14.2% and 34.9%, 26.3% with the addition of Al_2O_3 nano-particles respectively. The tribological properties of the composites could be improved. The friction coefficient was reduced by 22.5% by filling PTFE whereas the same property of Al_2O_3-filled composite was increased by 21.3%. The wear rate was reduced by 78.1% by filling PTFE and the same property was reduced by 94.1 % by filling Al_2O_3.
参考文献
| [1] | Rekha Rattan;J. Bijwe;M. Fahim .Influence of weave of carbon fabric on low amplitude oscillating wear performance of Polyetherimide composites[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2007(5/6):727-735. |
| [2] | J. Bijwe;S. Awtade;A. Ghosh .Influence of orientation and volume fraction of Aramid fabric on abrasive wear performance of polyethersulfone composites[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2006(4/5):401-411. |
| [3] | David L. Burris;W. Gregory Sawyer .Improved wear resistance in alumina-PTFE nanocomposites with irregular shaped nanoparticles[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2006(7/8):915-918. |
| [4] | Praveen Bhimaraj;David L. Burris;Jason Action;W. Gregory Sawyer;C. Gregory Toney;Richard W. Siegel;Linda S. Schadler .Effect of matrix morphology on the wear and friction behavior of alumina nanoparticle/poly(ethylene) terephthalate composites[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(9):1437-1443. |
| [5] | 李小慧,孙斓珲,杨振国.纳米氧化铝对聚甲醛力学性能及摩擦磨损性能的影响[J].机械工程材料,2007(05):62-65. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%