Dynamic Recrystallization and Precipitation Behavior of Mn-Cu-V Weathering Steel

材料科学技术（英文）, 2011, 27(12): 1131-1138.

^1, , ^2, , ^3,

1.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China

2.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China

3.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China

基金项目: the Doctorate Foundation of the Ministry of Education of China(20090042120005) The authors gratefully acknowledge the financial supports from the National Natural Science Foundation of China(51034009;;50974039)

Dynamic Recrystallization and Precipitation Behavior of Mn-Cu-V Weathering Steel

Hongyan Wu ^1, , Linxiu Du ^2, , Xianghua Liu ^3,

1.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China

2.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China

3.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, China

Keywords： Weathering steel

The hot deformation behavior of a Mn-Cu-V weathering steel was investigated at temperatures ranging from 850 to 1050℃ and strain rates ranging from 0.01 to 5 s-1 using MMS-300 thermal-mechanical simulator. The activation energy for dynamic recrystallization and stress exponent were calculated to be 551 kJ/mol and 7.73, respectively. The accurate values of critical strain were determined by the relationship between work hardening rate and flow stress (θ-σ) curves. The hyperbolic sine constitutive equation was employed to describe the relationship between the peak stress and Zener-Hollomon parameter during hot deformation. The interaction between dynamic recrystallization and dynamic precipitation of V(C,N) at a low strain rate was analyzed. The results showed that precipitation particles size of weathering steel increased with increasing strain at deformation temperature 950℃ and strain rate 0.1 s-1. The calculation results of the recrystallization driving force and pinning force showed that dynamic precipitation could retard the progress of dynamic recrystallization but not prevent it while the pinning forces is less than driving force. On the contrary, dynamic precipitation can effectively prevent the progress of dynamic recrystallization.

参考文献

[1]	S.F. Medina;M. Gomez;L. Rancel .Grain refinement by intragranular nucleation of ferrite in a high nitrogen content vanadium microalloyed steel[J].Scripta materialia,2008(12):1110-1113.
[2]	S. Shanmugam;R. D. K. Misra;T. Mannering;D. Panda;S.G. Jansto .Impact toughness and microstructure relationship in niobium- and vanadium-microalloyed steels processed with varied cooling rates to similar yield strength[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(2):436-445.
[3]	C. A. C. Imbert;H. J. McQueen .Peak strength, strain hardening and dynamic restoration of A2 and M2 tool steels in hot deformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):88-103.
[4]	S.F.MEDINA;C.A.HERNANDEZ .GENERAL EXPRESSION OF THE ZENER-HOLLOMON PARAMETER AS A FUNCTION OF THE CHEMICAL COMPOSITION OF LOW ALLOY AND MICROALLOYED STEELS[J].Acta materialia,1996(1):137-148.
[5]	B. DUTTA;E. J. PALMIERE;C. M. SELLARS .MODELLING THE KINETICS OF STRAIN INDUCED PRECIPITATION IN Nb MICROALLOYED STEELS[J].Acta materialia,2001(5):785-794.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Dynamic Recrystallization and Precipitation Behavior of Mn-Cu-V Weathering Steel

参考文献