对尺寸为φ4 mm×4.7 mm的压铸AZ91D镁合金铆钉热旋铆时的变形行为进行了数值模拟研究,采用了正交试验方法分析成形参数对铆钉成形的影响,得出最佳参数组合为:铆头初始温度为600℃,传热时间为2 s,铆头进给速度为0.8 mm/s,铆头转速为480 r/min.并分析不同成形参数下变形区温度、应力、应变分布规律及变形区的损伤情况,铆钉头部边缘处在成形中的等效应力最大,波动幅度显著,变形不稳定,且该区域成形后损伤最大,易产生破裂、褶皱等缺陷.
参考文献
| [1] | Asm International.Magnesium and Magnesium Alloy[M].Ohio:Metal Park,1999 |
| [2] | Blum W;Zhang P;Watzinger B et al.Comparative study of creep of the die-cast Mg-alloys AZ91,AS21,AS41,AM60 and AE42[J].Materials Science and Engineering A,2001,319-321:735-740. |
| [3] | Ninomiya R;Ojiro T;Kubota K .Improved heat resistance of Mg-Al alloys by the Ca addition[J].ACTA METALLURGICA ET MATERIALIA,1995,43(02):669-674. |
| [4] | 游国强 .一种轻合金热铆工艺[P].中国,200910103180.5,2009-07-22. |
| [5] | 余琨,黎文献,王日初,马正青.变形镁合金的研究、开发及应用[J].中国有色金属学报,2003(02):277-288. |
| [6] | 栾娜,李落星,李光耀,钟志华.AZ80镁合金的高温热压缩变形行为[J].中国有色金属学报,2007(10):1678-1684. |
| [7] | 余琨,黎文献.Mg-Al-Zn系变形镁合金轧制及热处理后的组织和性能[J].金属热处理,2002(05):8-11. |
| [8] | 李尚健.金属塑性成形过程模拟[M].北京:机械工业出版社,1999 |
| [9] | 游国强,左旭东,谭霞,王向杰,龙思远.压铸态AZ91D镁合金热压缩变形流变应力研究[J].稀有金属材料与工程,2013(09):1844-1848. |
| [10] | 丁文江.镁合金科学与技术[M].北京:科学出版社,2007 |
| [11] | 陈魁.试验设计与分析[M].北京:清华大学出版社,2005 |
| [12] | S.W. Xu;S. Kamado;N. Matsumoto;T. Honma;Y. Kojima .Recrystallization mechanism of as-cast AZ91 magnesium alloy duringhot compressive deformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):52-60. |
| [13] | 周德成 .摆动辗压变形时压力分布及主要变形特征的研究[J].机械工程学报,1991,27(06):38-43. |
| [14] | 李兵,游国强,龙思远,张百在,余亮.铝合金旋铆连接过程数值模拟分析[J].特种铸造及有色合金,2010(04):314-317. |
| [15] | C. D. Rans;R. C. Alderliesten;P. V. Straznicky .Assessing the effects of riveting induced residual stresses on fatigue crack behaviour in lap joints by means of fractography[J].International Journal of Fatigue,2009(2):300-308. |
| [16] | Mark Denis Nave;Matthew Robert Barnett .Microstructures and textures of pure magnesium deformed in plane-strain compression[J].Scripta materialia,2004(9):881-885. |
| [17] | 张岐良,曹增强,秦龙刚,陈允全.钛合金电磁铆接数值模拟[J].稀有金属材料与工程,2013(09):1832-1837. |
| [18] | Gourdet S;Montheillet F .An experimental study of the recrystallization mechanism during hot deformation of aluminium[J].Materials Science and Engineering A,2000,283(1/2):274-288. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%