以三亚甲基碳酸酯(TMC)为单体,辛酸亚锡为催化剂,通过开环聚合反应制备了聚三亚甲基碳酸酯(PTMC).利用核磁共振分析(1H-NMR)对PTMC的结构进行了验证;利用差示扫描量热(DSC)和热重分析(TG)对PTMC的热性能进行了测试;利用乌氏黏度计测定了PTMC的特性黏度,并研究了PTMC的特性黏度与数均分子量Mn之间的关系.结果表明,PTMC是一种在室温下呈橡胶态的无定型聚合物,其开始失重的温度在280℃以上,并且受分子量影响较小;可以通过改变单体与催化剂的摩尔比例([M]/[C])来调整PTMC的Mn随着[M]/[C]比值的增大,Mn在增大.
参考文献
| [1] | Liqiong Liao;Chao Zhang;Shaoqin Gong .Preparation of poly(trimethylene carbonate)-block-poly(ethylene glycol)-block-poly(trimethylene carbonate) triblock copolymers under microwave irradiation[J].Reactive & functional polymers,2008(3):751-758. |
| [2] | Liao LQ;Zhang C;Gong SQ .Rapid synthesis of poly(trimethylene carbonate) by microwave-assisted ring-opening polymerization[J].European Polymer Journal,2007(10):4289-4296. |
| [3] | Zhang Z;Grijpma DW;Feijen J .Poly(trimethylene carbonate) and monomethoxy poly(ethylene glycol)-block-poly(trimethylene carbonate) nanoparticles for the controlled release of dexamethasone[J].Journal of Controlled Release: Official Journal of the Controlled Release Society,2006(3):263-270. |
| [4] | Watanabe J;Amemori S;Akashi M .Disparate polymerization facilitates the synthesis of versatile block copolymers from poly(trimethylene carbonate)[J].Polymer: The International Journal for the Science and Technology of Polymers,2008(17):3709-3715. |
| [5] | Habraken WJ;Zhang Z;Wolke JG;Grijpma DW;Mikos AG;Feijen J;Jansen JA .Introduction of enzymatically degradable poly(trimethylene carbonate) microspheres into an injectable calcium phosphate cement.[J].Biomaterials,2008(16):2464-2476. |
| [6] | Zhang Z;Kuijer R;Bulstra SK;Grijpma DW;Feijen J .The in vivo and in vitro degradation behavior of poly(trimethylene carbonate)[J].Biomaterials,2006(9):1741-1748. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%