引入不同引发剂对马来酸酐接枝改性废旧橡胶粉制备橡胶混凝土，对其坍落度、抗压强度、动弹性模量等性能进行研究，并通过SEM对其界面结合进行分析。试验结果表明，以DCP、BPO作为引发剂马来酸酐在橡胶表面均有接枝现象，但DCP效果明显，且接枝率最高。 DCP作为引发剂对应改性橡胶混凝土28 d抗压强度明显优于另外两种改性剂，且橡胶最佳掺量为15%时，强度达到最大值45.1 MPa。 DCP作为引发剂的改性橡胶混凝土中界面周围有很多针状和片状水泥水化物穿插嵌入橡胶，两物相界面结合牢固紧密，效果最佳。
Properties of slump, compressive strength, dynamic modulus of elasticity, etc, of rubber concrete with waste rubber powder modified by MAH with different initiating agents, and analysis of the interface bonding with SEM. The results show that DCP, BPO as initiators were grafted on the rubber surface, but the effect of DCP was obvious, and the grafting rate was the highest. 28 d compressive strength of modified rubber concrete was better than the other two kinds of initiators. Maximum strength was 45 . 1 MPa when the best radio was 15%. There were a lot of needle and flake cement hydrates embedded in the rubber around modified rubber concrete interface when DCP as initiator, tied the two phase interfaces, the best effect.
参考文献
| [1] | 张艳聪;申俊敏;高玲玲.废旧轮胎胶粉混凝土的路用性能试验研究[J].混凝土,2014(10):57-59,62. |
| [2] | 薛刚;侯帅.不同水胶比的塑钢纤维橡胶混凝土力学性能研究[J].硅酸盐通报,2016(5):1552-1557. |
| [3] | 王刚;杨慧;张磊.橡胶粒径对橡胶混凝土抗压强度的影响[J].路基工程,2011(1):128-130. |
| [4] | 赵朋斌 .橡胶集料混凝土的碳化试验研究[D].天津大学,2012. |
| [5] | 王宝民;刘伟.国外掺废旧橡胶颗粒水泥混凝土研究进展[J].混凝土,2010(4):54-56,103. |
| [6] | 张海波;管学茂;刘小星;李飞.废旧橡胶颗粒对混凝土强度的影响及界面分析[J].材料导报,2009(8):65-67. |
| [7] | 董智贤;贾德民;周彦豪;潘锦秀;徐志明.马来酸酐改性天然胶乳的制备及应用[J].合成橡胶工业,2005(3):200-204. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%