某滨海火力发电厂钢结构关键部位采用复层矿脂包覆技术进行腐蚀防护。通过中性盐雾试验和电化学试验研究了防蚀膏和防蚀带对对碳钢的防腐蚀效果，并介绍了该技术在滨海电厂钢结构关键部位的施工工艺和应用情况。盐雾试验和电化学试验结果表明，防蚀膏和防蚀带具有优良的耐盐雾和耐氯离子渗透性能。通过在滨海电厂钢结构关键部位的实际应用证明了其具有良好的防腐蚀性能。
Key parts of steel structure in a coastal power plant are coated with multilayer petrolatum coating. Salt spray test and electrochemical impedance spectroscopy （EIS） technology were used to study the anti-corrosion ability of anti-corrosion petrolatum grease and anti-corrosion tape. Applications of multilayer petrolatum coated anti-corrosion system were discussed, and the process of the technology was also introduced. The results of salt spray test and EIS showed that the anti-corrosion petrolatum grease and anti-corrosion tape had high obstructive capacity for H2O, O2 and Cl . The results of this project also illuminate that multilayer petrolatum coated anti-corrosion system is a reliable and advanced technology.
参考文献
| [1] | 马永新.钢结构防腐蚀涂料施工技术[J].上海涂料,2010(07):51-53. |
| [2] | 王军,付强,闫雪峰.我国跨海大桥钢结构防腐保护与涂装[J].现代涂料与涂装,2008(10):37-41. |
| [3] | 侯保荣.钢铁设施在海洋浪花飞溅区的腐蚀行为及其新型包覆防护技术[J].腐蚀与防护,2007(04):174-175,187. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%