By testing the melt index (MI), tensile strength and breaking extension ratio, the thermal ageing rate of polyoxymethylene (POM) was analyzed and compared. The surface morphology and type of function group of POM surface were observed and analyzed by SEM and XPS. The results show that the MI value increases gradually with the ageing time at 120 ℃, indicating that the thermal oxidation decomposition occurrs slowly. The effect of 20-day thermal ageing on the tensile strength and breaking extension ratio of POM is not obvious, showing that the ageing of POM is quite a long process. After 105-day, thermal ageing cracking and powdering occurr on the POM surface. XPS determination shows the C1s spectra of samples before and after ageing include two peaks of C-C and C-O, while after ageing the content of C-C decreases and the content of C-O increases, indicating that the thermal ageing of POM is mainly the breaking and decomposing of C-C bond. The O1s/C1s ratio of original samples is 56.98% and after 105-day thermal ageing the ratio is 72.92%.
参考文献
| [1] | 窦强,冯新,陆小华.聚甲醛自润滑复合材料的开发与应用[J].高分子材料科学与工程,2003(01):36-40. |
| [2] | QU Qingwen;LI Xiaojiang;ZHU Jun .Sliding Bearing Research of Universal Coupling of Automobile[J].Lubrication and Sealing,1996,5:58-60. |
| [3] | HU Ping;HUANG Chou;ZHENG Hua.Study on Application of Polyester Elastomer in Automobile Steering Systems[J].Automobile Technology,2003(08):32-34. |
| [4] | Schweitzer C E;Macdonal R N;Punderson J O .Thermally Stable High Molecular Weight Polyoxymethylenes[J].Journal of Applied Polymer Science,1959,1(02):158-163. |
| [5] | 施立新.均聚甲醛降解问题的探讨[J].上饶师范学院学报,2001(03):47-49. |
| [6] | YU Jian.The Ageing Behavior of POM in Boiling Water[J].China Plastics,1996(01):17-21. |
| [7] | ZHOU Dage;XIE Gecheng.The Ageing and Resistance Technology to Ageing of Plastics[M].北京:化学工业出版社,2002 |
| [8] | JI Kejian.Advances in XPS Applied to Surface Degradation of Polymers[J].Polymer Materials Science and Engineering,1994(05):12-17. |
| [9] | SU Chengwei;ZHANG Dezheng;XU Zhongde et al.The Thermalgravimetric Investigation of Polyoxymethylene[J].FunctionalPolymer,1994,2:165-172. |
| [10] | R Stohler;k Berger .Die Angewandte Makromolekulare Chemie[J].Macromolecular Materials and Engineering,1990,176-177:323. |
| [11] | ZHOU Dagang;XIE Gecheng.Plastics Ageing and Ageing Resistance Technology[M].北京:中国轻工业出版社,1998 |
| [12] | ZHONG Shiyun;XU Wei;WANG Gongshan.Decomposition and Stability of Polymer[M].北京:化学工业出版社,2002 |
| [13] | HE Chunxia;SHI Liping .Wear Resistance Property of POM Etc[J].Machine Design and Manutacturing Engineering,1998,6:48-50. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%