The new preparation method of scandium-bearing master alloys, in which scandium oxide was fluorinated by reaction with NH4HF2 and then reduced by aluminum-magnesium in fused salt containing alkali and alkaline fluoride under atmosphere, was studied. The effect of sorts of metallic reductive and technique conditions such as reducing temperature and time on the recovery of Sc was discussed. When the liquid aluminum-magnesium was used as the reductive agent, the all-recovery exceeds 80% and the concentration of Sc in master alloy prepared exceeds 1.9%. The best reducing reaction temperature and time are 1100 K and 40 min respectively. The newly produced Sc from reduction combines with Al to produce the stable compound Al3Sc, so the reduction progress is sustained and the recovery of Sc is increased.
参考文献
| [1] | Filatov Yu A;Yelagin V I;Zakharov V V .New Al-Mg-Sc alloys[J].Materials Science and Engineering,2000,A280:97. |
| [2] | Yin Zhimin;Pan Qinglin;Zhang Yonghong et al.Effect of minor Sc and Zr on the microstructure and mechnical properties of Al-Mg based alloys[J].Materials Science and Engineering,2000,A280:151. |
| [3] | Yin Zhimin;Jiang Feng;Yang Qinglin.Effect of minor Sc and Zr on the microstructure and mechnical properties of Al-Zn-Mg based alloys[J].Trans Nonferrous Met Soc China,2000(A280):151. |
| [4] | Li Hanguang;Yin Zhiming;Jiang Feng.A change from the predominance in Sc resourses into one in the technology of the further process of Sc product in China[C].Development about Rare Earth Science and Technology,2000:241. |
| [5] | Jiang Feng;Yin Zhinming;Li Hanguang .Preparation methods of scandium-bearing mster alloys[J].Chinese Rare Earths,2001,22(01):41. |
| [6] | Lu Guimin;Liu Xueshan .Preparation of Al-Sc master alloy by aluminathermy in nNaF*AF3 molten salt[J].The Chinese Journal of Nonferrous Metals,1999,9(01):171. |
| [7] | Yang Qingshan;Liu Shupin;Liu Shizhong .Tendency of preparation method and S & D of Al-Sc alloy[J].Hunan Rare Earth,2002,58(02):17. |
| [8] | Wu Jiangshe;Zuo Jianshe;Reng Jianshe .Preparation Al-Sc master alloy by scandium fluerid-aluminathermy[J].Hunan Rare Earth,2001,55(03):12. |
| [9] | 姜锋,尹志民,李汉广,潘青林,彭志辉,阿列克桑德夫斯基СВ,拉特涅尔·A·X.氧化钪-氯化-铝镁热还原法制备钪中间合金新工艺研究[J].稀土,2001(03):34-36. |
| [10] | 孙本良,翟玉春,田彦文.氟盐体系中电解制取铝钪合金的研究[J].稀有金属,1998(03):191-194. |
| [11] | HuHuaye .Peparation of high purity scandium metal[J].Chinese Rare Earths,1999,20(04):70. |
| [12] | Murray J L .The Al-Sc (aluminum-scandium ) system[J].Journal of Phase Equilibria,1998,19(04):380. |
| [13] | Alexander Pisch;Rainer Schmid Fetzer;Gabriele Cacciamani et al.Mg-rich phase equilibria and thermodynamic assessment of the Mg-Sc system[J].Zeitschrift fur Metallkunde,1998,89(07):474. |
| [14] | Alexander Pisch;Joachim Grobner;Rainer Schmid-Fetzer .Application of computational thermochemitry to Al and Mg alloy processing with Sc additiong[J].Materials Science and Engineering,2000,A289(12):3. |
| [15] | Ratner A H;Geilikman M B;Aleksandrovski S V et al.Thermodynamic caculation on metallic thermoreduction during preparation of aluminum-rare earth master alloys[J].Transactions of Nonferrous Metals Society of China,2001,11(01):18. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%