通过对Ti-2.5Cu,Ti-3Fe,Ti-3Cr钛合金进行微区成分和宏观成分的对比研究,得出了3种合金铸锭中合金元素宏观和微观偏析规律.在等轴晶内,3种元素含量均沿晶粒生长方向增加,其中Cu,Fe元素偏析明显,Cr元素偏析程度小;柱状晶内,Cu,Fe,Cr的含量均沿晶粒生长方向增加,但偏析均不明显;晶界处的平均Cu,Fe含量明显低于晶内,而Cr含量则远远高于晶内,Cr在晶界偏析明显.宏观方面,3种元素均向铸锭的顶部和中心富集,其中Cu和Fe的偏析程度较大而Cr的偏析程度小,径向的偏析程度比轴向严重.
参考文献
| [1] | 王金友;葛志明;周彦邦.Titanium Alloys for Aero Application(航空用钛合金)[M].上海:上海科学技术出版社,1985:223-227. |
| [2] | A Mitchell;D W Tripp.HID and HDI Dissolution During Titanium Melting Processes[A].Adenauerllee: Federal,1993:2257-2264. |
| [3] | Bellot J P;Hans S;Hess E.The Formation and Removal of"Hard-Alpha"Material During the Melting of Titanium Alloys[A].Adenauerllee: Federal:1454-1461. |
| [4] | Eschenbach R C;Schlienger M E;Haun R E.Recent Improve ments in the Economics of Plasma Melting[A].Adenauerllee: Federal,1993:2301-2307. |
| [5] | Bomerger H B.Alpha Segregation in Titanium Alloys[A].New York: American Institute of Mining, Matellurgy, and Petroleum,1981:2197-2202. |
| [6] | Blenkinsop P A.High Temperature Titanium Alloys the Metallurfical Understanding, Development and Achievements of Conventional Alloys[A].Tokoy:Japan Institute of Metals,1993:1861-1868. |
| [7] | 蔡学章;李平全;窦永庆.Solidifying Segregation ofTi-2.5Cu AlloyIngot[A].Beijing:General Research Institutefor Nonferrous Metals,1983:25-30. |
| [8] | 窦永庆;高颀;王镐.The Control of Segregation of Fe in φ51 8 mm Ti-1023 Alloy Ingot[A].Changsha:Central SouthUniversity of Technology,1990:18-21. |
| [9] | 窦永庆.The Contribution of Main Alloy Elements in Titanium Alloy Ingots[A].北京:原子能出版社,1987:43-48. |
| [10] | 曾泉浦.SegregationinTitaniumAlloyIngotsby VAR[J].钛工业进展,1994(03):9-11. |
| [11] | 周尧和;胡状麒;介万奇.凝固技术[M].北京:机械工业出版社,1998:11-17. |
| [12] | 葛志明.钛的二元系相图[M].北京:国防工业出版社,1991:21-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%