对机械镀锌层分别用三价铬、稀土和六价铬进行了钝化处理,利用盐雾试验和电化学测试对不同钝化膜的耐蚀性与电化学行为进行了比较研究.盐雾试验结果表明,稀土与三价铬钝化处理的效果均已超过传统的六价铬钝化,比六价铬钝化膜的耐蚀性提高了一倍以上;稀土钝化膜的耐蚀性最好,三价铬钝化膜的耐蚀性仅次于稀土钝化膜的.电化学测试表明,三价铬、稀土和六价铬钝化膜都能够不同程度地抑制腐蚀的阴极电极反应,抑制阴极反应程度最大的是稀土钝化膜,其次是三价铬钝化膜,最小的是六价铬钝化膜.三价铬与稀土钝化工艺的环保和良好的防腐效果使其具有良好的应用前景.
The mechanically plated zinc coating was passivated with chemicals containing trivalent chromi-um,rare earth metal and hexavalent chromium respectively.Then the corrosion resistance and electrochemi-cal behavior of the passivated coatings were compared by salt spay test and electrochemical test.The result of salt spay test showed that the coatings passivated with trivalent chromium and rare earth metal are superi-or to that with hexavalent chromium by one fold in corrosion resistance.The coating passivated with rare earth metal Was the best in corrosion resistance and that with trivalent chromium was the next.The electro-chemical test showed that all the passivation treatments with trivalent chromium,rare earth metal and hexa-valent chromium could suppress the cathode reactions to some extent.The effectiveness of passivation chem-icals in suppression of the cathodic reaction might be ranking as follows:rare earth metal,trivalent chromi-um.and hexavalent chromiam.Therefore,chemicals containing trivalent chromiam and rare earth metal had good application foreground for their good corrosion resistance and environmental-friendly.
参考文献
| [1] | 丁金城,毕玉遂,赵增典,等.高速公路护栏螺栓机械镀Zn生产工艺[J].腐蚀科学与防护技术,2002,14(1):60. |
| [2] | 欧家才,刘钧泉.我国法律及标准对氰化物和六价铬排放的要求[J].电镀与涂饰,2007,26(8):51. |
| [3] | 邹锦光,刘建平,曾振欧,等.镀锌层的三价铬钝化[J].电镀与涂饰,2005,24(8):46. |
| [4] | 胡立新,兰林,朱中兵,等.镀锌层三价铬高耐蚀蓝白钝化工艺研究[J].材料保护,2005,38(7):25. |
| [5] | Bethencourt M,Botana F J,Calvino J J,et al.Lanthanide com-pounds as environmentally-friendly corrosion inhibitors of alu-minium alloys:a review[J].Corrosion Science,1998,40(11):1803. |
| [6] | 吕雪飞,李淑英.稀土对金属表面钝化作用研究进展[J].电镀与涂饰,2006,25(10):46. |
| [7] | 巴晓革,赵增典,丁金城.机械镀的镀层形貌及耐蚀性[J].腐蚀与防护,2007,28(6):293. |
| [8] | GB/T10125-1997.人造气氛腐蚀试验盐雾试验方法[S].1997. |
| [9] | 沈品华,屠振密.电镀锌及锌合金[M].北京,机械工业出版社,2001.65. |
| [10] | 吴纯素.化学转化膜[M].北京:化学工业出版社,1989.95. |
| [11] | 沈品华.镀锌三价铬钝化[J].电镀与环保,2007,27(3):27. |
| [12] | Hinton B R W,Wilson L.The corrosion inhibition of zinc with cerous chloride[J].Corrosion Science,1989,29(8):967. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%