本文研究了低Cr2O3含量Al2O3-MgO浇注料的物理性能,采用X射线衍射仪和扫描电子显微镜对浇注料的物相变化和显微结构进行了分析.结果发现:镁铝尖晶石含量可控制浇注料的显气孔率、体积密度、线变化率及强度.高温下Cr2O3消失是因为其固溶于新生成的MgAl2O4相中,固溶的存在提高了浇注料的物理性能.采用硅微粉结合时,高温下会产生一定的镁橄榄石相.
参考文献
| [1] | Filippo Cirilli;Mario Tonelli .Mathematical Modelling of Magnesia Carbon Refractories Reactions with Steel[J].Steel Research International,2006(4):250-255. |
| [2] | Haq M I U;Khanna R;Koshy P et al.Recycling alumina-carbon refractory waste in steelmaking:Mechanisms of refractory degradation[J].AISTech-Iron and Steel Technology Conference Proceedings,2009,1:1067-1076. |
| [3] | 陈肇友.RH精炼炉用耐火材料及提高其寿命的途径[J].耐火材料,2009(02):81-95. |
| [4] | Sokolov V A;Malysheva T Y .The structure of fusion-cast high-chrome oxide refractories in the Cr2O3-MgO-Al2O3 system[J].Refractories and Industrial Ceramics,2005,46(02):127-131. |
| [5] | 高里存,张强.镁铝尖晶石和铬矿对镁质浇注料烧结的影响[J].耐火材料,2007(01):54-55,58. |
| [6] | Sarkar R;Kumar D S;Banerjee G .Effect of addition of Cr2O3 on the properties of reaction sintered MgO-Al2O3 spinels[J].Journal of the European Ceramic Society,2002,22(08):1243-1250. |
| [7] | Jo S K;Song B;Kim S H .Thermodynamics on the formation of spinel (MgO@Al2O3) inclusion in liquid iron containing chromium[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,2002,33(05):703-709. |
| [8] | Turkin, AI;Drebushchak, VA .Solid solutions in the MgO-Al2O3-Cr2O3 system[J].Journal of thermal analysis and calorimetry,2009(1):81-86. |
| [9] | 李龙,于景坤,邹宗树.含铬耐火材料及其在冶金中的应用[J].中国冶金,2008(06):11-16,20. |
| [10] | 李享成,朱伯铨.镁砂和硅微粉加入量对Al2O3-尖晶石浇注料性能的影响[J].钢铁研究,2001(06):15-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%