采用射频磁控溅射法在Si(100)基片上制备了NiZn铁氧体薄膜,研究了退火温度对薄膜性能的影响.采用XRD分析仪分析了薄膜的相结构,原子力显微镜分析了薄膜的表面形貌,振动样品磁强计测量了薄膜的磁性能,结果表明,随着退火温度的升高,薄膜的结晶状态越好,晶粒尺寸越大,饱和磁感应强度越高,面内矫顽力越小.
NiZn ferrite thin films are prepared on single-crystal Si(100) substrate by radio frequency(RF) magnetron sputtering technique.The structure and magnetic properties of the deposited films is investigated as a function of annealing temperature.The crystal structure of deposited films was investigated by the X-ray diffraction(XRD) with Cu K( radiation,and the surface morphologies(RMS) of deposited films is analyzed by atom force microscopy(AFM),and the magnetic properties in the plane of deposited films are measured at room temperature using the vibrating sample magnetometer(VSM)as well.Results show that with the increase of annealing temperature,the state of crystallization is better,the grain size is larger,saturation magnetization is higher and coercivity in plane is lower.
参考文献
| [1] | 黄永杰;李世堃;兰中文.磁性材料[M].成都:电子科技大学出版社,1993:11. |
| [2] | Dorsey PC.;Grabowski KS.;Lubitz P.;Chrisey DB.;Horwitz JS.;Rappoli BJ. .STRESS-INDUCED MAGNETIC ANISOTROPY IN THICK ORIENTED NIZN-FERRITE FILMS ON (100) MGO SUBSTRATES[J].Journal of Applied Physics,1997(10):6884-6891. |
| [3] | Zhenghong Qian;Geng Wang .NiZn ferrite thin films prepared by Facing Target Sputtering[J].IEEE Transactions on Magnetics,1997(5):3748-3750. |
| [4] | Jianhua Gao;Yitao Cui;Zheng Yang .The magnetic properties of Ni_xZn_(1-x)Fe_2O_4 films fabricated by alternative sputtering technology[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2004(2):111-114. |
| [5] | Desai M.;Prasad S.;Venkataramani N.;Samajdar I.;Nigam AK.;Keller N. Krishnan R.;Baggio-Saitovitch EM.;Pujada BR.;Rossi A. .Anomalous variation of coercivity with annealing in nanocrystalline NiZn ferrite films[J].Journal of Applied Physics,2002(10 Pt.2):7592-7594. |
| [6] | Tanaka T;Kurisu H;Matsuura M;Shimosato Y;Okada S .Fabrication of ultrathin Ni-Zn ferrite films using electron cyclotron resonance sputtering method[J].Journal of Applied Physics,2006(8):N8507-1-N8507-3-0. |
| [7] | 奚小网,陈亚杰.脉冲激光沉积NiZn铁氧体薄膜的微观结构和磁性[J].真空科学与技术学报,2003(03):195-198,211. |
| [8] | 潘维国;曹起骧;马喜腾 等.核电用钢静态再结晶晶粒尺寸及其变化规律的模型研究[J].塑性工程学报,1998,5(04):17. |
| [9] | Dash J;Prasad S;Venkataramani N et al.Study of magnetizaton and crystallization in sputter deposited LiZn ferrite thin films[J].Journal of Applied Physics,1999,86(06):3303. |
| [10] | Desai M.;Samajdar I.;Venkataramani N.;Prasad S.;Kishan P. Kumar N.;Dash J. .A TEM study on lithium zinc ferrite thin films and the microstructure correlation with the magnetic properties[J].Journal of Magnetism and Magnetic Materials,2001(1):108-112. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%