为了提高C/C复合材料的抗高温氧化性能,用包埋法在C/C复合材料表面制备SiC内涂层,再在其上刷涂制备Y2O3-ZrO2-Al2O3多组分涂层,对制备涂层的各种影响因素进行分析,确定最佳制备工艺,并考察了该涂层的组织结构和抗高温氧化性能.结果表明:最佳制备条件为以SiC为内涂层、10％聚乙烯醇(PVA)为分散剂,以Y2O3,ZrO2,Al2O3,Si及C为原料,室温涂覆,升温到1 873 K保温30 min,反复进行5次;该涂层在1 873 K下氧化19 h,失重率仅1.76％,有良好的短期抗高温氧化性能,氧化29 h时失重率为6.23％,涂层可能已破坏失效;涂层的失效是由于其表面形成的孔洞和裂纹不能愈合而导致的.
参考文献
| [1] | 邓世均.高性能陶瓷涂层[M].北京:化学工业出版社,2002:181~184.,2002. |
| [2] | Ahmet P,Ozkan S,Erdal C .Effects of porosity on thermal loadings of functionally graded Y2O3-ZrO2/NiCoCrAlY coatings[J].Materials and Design,2002,23 |
| [3] | Federico S,Monica F,Milena S .Multilayer coating with self-sealing properties for carbon-carbon composites[J].Carbon,2003,41 |
| [4] | Federico S,Milena S,Monica F .Oxidation protective multilayer coatings for carbon-carbon composites[J].Carbon,2002,40 |
| [5] | HuangJF,LiHJ,ZengXR,etal .ZrO2-SiO2 gradient multilayer oxidation protective coating for SiC coated carbon/carbon composites[J].Surface and Coatings Technology,2005,190 |
| [6] | Huang J F,Li H J,Zeng X R,et al .Yttrium silicate oxidation protective coating for SiC coated carbon/carbon composites[J].Ceramics International,2006,32 |
| [7] | 焦更生,李贺军,卢国锋.碳纤维增强碳复合材料表面多层复合涂层中SiC和TiC内层的比较[J].硅酸盐学报,2010(10):2014-2020. |
| [8] | 马彦龙,张凯莉,侯文生,戴晋明,王帅,范海宾.聚乙烯醇水溶液对多壁碳纳米管分散性的研究[J].精细石油化工进展,2011(05):32-34,51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%