研究了超声处理对铸态及均匀化处理后7050铝合金显微组织的影响,并采用高温压缩模拟试验对在300～450℃、应变速率为2.77×10-4～2.77×10-2 s-1条件下常规与超声铸造7050合金均匀化后的塑性变形行为进行了研究.结果表明:相同条件热变形后,超声铸造铝合金的晶粒比常规铸造的细小;在相同变形条件下,超声铸造合金的流变应力明显要小;超声铸造合金的热变形激活能为136 kJ·mol-1,低于常规铸造的155 kJ·mol-1,更易热变形.
参考文献
| [1] | J. D. Robson .A new model for prediction of dispersoid precipitation in aluminium alloys containing zirconium and scandium[J].Acta materialia,2004(6):1409-1421. |
| [2] | Spigarelli S. .Interpretation of creep behaviour of dispersion-strengthened Al-Fe-V-Si alloys in terms of detachment mechanisms: an overview[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):306-314. |
| [3] | Cerri E.;Forcellese A.;Mcqueen HJ.;Evangelista E. .COMPARATIVE HOT WORKABILITY OF 7012 AND 7075 ALLOYS AFTER DIFFERENT PRETREATMENTS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(2):181-198. |
| [4] | 林高用,张辉,郭武超,彭大暑.7075铝合金热压缩变形流变应力[J].中国有色金属学报,2001(03):412-415. |
| [5] | 沈键 .2091铝锂合金高温塑性变形行为研究[D].中南工业大学,1996. |
| [6] | Yao XX.;Hutchinson B.;Zajac S. .The strain-rate sensitivity of flow stress and work-hardening rate in a hot deformed Al-1.0Mg alloy[J].Journal of Materials Science Letters,2000(9):743-744. |
| [7] | Shi H;McLaren AJ;Sellars CM;Shahani R;Bolingbroke R .Constitutive equations for high temperature flow stress of aluminium alloys[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1997(3):210-216. |
| [8] | 马英义,宛亚坤,王景新.6082铝合金热轧工艺研究[J].轻合金加工技术,2000(06):11-12,33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%