采用场发扫描电镜和EPMA电子探针研究了C-Si-Mn系双相钢锰配分行为及其对马氏体形貌、体积分数和力学性能的影响.结果表明:试验用钢0.20C-1.28Mn-0.37Si在经双相区热处理后,在720℃的淬火温度下,随着保温时间的延长,锰元素由铁素体向奥氏体中的配分量不断增加,达到化学势平衡(即饱和状态)所需的保温时间为1500s;马氏体体积分数随着保温时间的延长而增加,达到饱和的时间是1 300 s;抗拉强度随着保温时间的延长而升高,当达到某一时间时,抗拉强度保持恒定.
参考文献
| [1] | Bhattacharya D .Developments in Advanced High Strength Steels[J].Iron and Steel,2005,40(Supplement):69. |
| [2] | Hodgson P D;Zahiri S H;Whale J J et al.The Static and Metadynamic Recrystallization Behavior of an X60 Nb Microalloyed Steel[J].ISIJ International,2004,44(07):1224. |
| [3] | Yuki TOJI;Takako YAMASHITA;Katsumi NAKAJIMA .Effect of Mn Partitioning during Intercritical Annealing on Following γ->α Transformation and Resultant Mechanical Properties of Cold-rolled Dual Phase Steels[J].ISIJ International,2011(5):818-825. |
| [4] | Erdogan M .Effect of Austenite Dispersion on Phase Transformationin Dual Phase Steel[J].Scripta Materialia,2003,48(05):501. |
| [5] | Mehmet Erdogan;Suleyman Tekeli .The effect of martensite volume fraction and particle size on the tensile properties of a surface-carburized AISI 8620 steel with a dual-phase core microstructure[J].Materials Characterization,2002(5):445-454. |
| [6] | 苏钰,符仁钰,李麟.马氏体含量对St12Q1和St37-2G双相钢力学性能的影响[J].上海金属,2004(04):8-12. |
| [7] | 温东辉.金相组织对双相钢强度影响的研究[J].上海金属,2005(06):51-55. |
| [8] | 张增良,宋仁伯,程知松,赵爱民,赵征志,刘光明,熊爱明.连续退火工艺和合金元素对800 MPa级冷轧双相钢组织性能的影响[J].热加工工艺,2008(06):27-29,33. |
| [9] | 潘恩宝,邸洪双,蒋光炜,鲍成人.奥氏体化时间对DP780冷轧双相钢组织和性能的影响[J].特殊钢,2010(05):58-60. |
| [10] | 赵征志,牛枫,唐荻,赵爱民,金光灿.超高强度冷轧双相钢组织与性能[J].北京科技大学学报,2010(10):1287-1291. |
| [11] | 邝霜,康永林,于浩,刘仁东,严玲.冷轧双相钢连续退火组织的转变[J].钢铁,2007(11):65-68,73. |
| [12] | 邝霜,康永林,于浩,齐秀美,刘仁东.Fe-C-Mn系冷轧双相钢两相区奥氏体化过程模拟[J].北京科技大学学报,2008(08):858-863. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%