对00Cr22Ni5Mo3N热轧板卷热卷取工艺进行了模拟试验,结果表明:卷取温度对00Cr22Ni5Mo3N钢的冲击韧性有显著影响,随着卷取温度的提高,钢的韧性逐渐降低,其最佳热卷取温度为550～600℃.在较高的卷取温度下CrN、Cr2N、Cr2(C,N)、χ相和σ相的析出是导致模拟试样冲击韧性降低的主要原因.
参考文献
| [1] | 王一德,李国平,王立新,李志斌.00Cr22Ni5Mo3N双相不锈钢板材的生产工艺[J].特殊钢,2001(05):36-37. |
| [2] | 葛冬平 .宝钢试制成功高强度双相不锈钢2205热轧带钢[N].宝钢日报,2007-01-05. |
| [3] | S S M Tavaresa;R F de Noronhaa;M R da Silvab et al.475℃ Embrittlement in a Duplex Stainless Steel UNS S31803[J].Materials Research,2001,4(04):237. |
| [4] | K.L. Weng;H.R. Chen;J.R. Yang .The low-temperature aging embrittlement in a 2205 duplex stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):119-132. |
| [5] | Guenter Herbsleb;Paul Schwaab.Precipitation of Intermetallic Compounds,Nitrodes and Carbides in AF 22 Duplex Steel and Their Influence on Corrosion Behavior in Aeids[A].Materials Park:American Society for Metals,1983:15. |
| [6] | 吴玖.双相不锈钢[M].北京:冶金工业出版社,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%