基于连续介质损伤力学理论,引入表征材料内部微细缺陷的损伤变量,导出了三维复合材料厚壁圆筒的损伤模型,预测该结构内各处的损伤过程;针对不同损伤模式,推导出包含不同结合力和损伤变量的损伤扩展准则;利用三维有限元分析软件模拟计算出结构损伤破坏的全过程,分析了复合材料圆筒的损伤模式与破坏机理,以及能量变化关系。
Based on the CDM theory,damage models are proposed to predict the progressive failure properties of thick-wall tube of the steel-carbon fiber/epoxy composite.Internal damage variables were introduced in order to quantify damage concentration associated with each possible failure mode during the damage process.A 3D finite element technique is adopted to perform the progressive failure analysis.The material model has been implemented into ABAQUS explicit finite element code within solid elements and the computed result has proven to be capable of reproducing experimental results with good accuracy in terms of static responses,energy dissipation and extent of damage.This work provides a progressive understanding of the damage initiation and propagation behaviors of composite laminated cylindrical structures above.
参考文献
| [1] | 杜善义.先进复合材料与航空航天[J].复合材料学报,2007(01):1-12. |
| [2] | Kashtalyan M.;Soutis C. .Analysis of local delaminations in composite laminates with angle-ply matrix cracks[J].International Journal of Solids and Structures,2002(6):1515-1537. |
| [3] | Talreja R .Transverse cracking and stiffness reduction in composite laminates[J].Journal of Composite Materials,1985,19(04):355-375. |
| [4] | Dharani LR;Tang H .Micromechanics characterization of sub laminate damage[J].International Journal of Fracture,1990,46(02):123-140. |
| [5] | A. Plumtree;M. Melo;J. Dahl .Damage evolution in a [±45]_(2S) CFRP laminate under block loading conditions[J].International Journal of Fatigue,2010(1):139-145. |
| [6] | Damage characterization of a cross-ply carbon fiber/epoxy laminate by an optical measurement of the displacement field[J].Composites science and technology,2010(1):94. |
| [7] | 冯培锋,王殿富,杜善义,李海涛.复合材料层板基于剩余刚度比的剩余强度模型[J].应用力学学报,2001(01):40-44. |
| [8] | P. Maimi;P.P. Camanho;J.A. Mayugo;C.G. Davila .A continuum damage model for composite laminates: Part Ⅰ - Constitutive model[J].Mechanics of materials,2007(10):897-908. |
| [9] | Bianchi S;Corigliano A;Frassine R et al.Modelling of interlaminar fracture process in composite using interface elements[J].Composites Science and Technology,2006,66:255-263. |
| [10] | M.V. Donadon;L. Iannucci;B.G. Falzon;J.M. Hodgkinson;S.F.M. de Almeida .A progressive failure model for composite laminates subjected to low velocity impact damage[J].Computers & structures,2008(11/12):1232-1252. |
| [11] | Donadon MV .The structural behavior of composite laminates manufactured using resin infusion under flexible tooling (RIFT) process[D].Department of Aeronautics,Imperial College London,2005. |
| [12] | Hashin Z .Failure criteria for unidirectional fiber composites[J].Journal of Applied Mechanics,Transactions of the ASME,1980,47:329-334. |
| [13] | A. Puck;H. Schurmann .Failure analysis of FRP laminates by means of physically based phenomenological models[J].Composites science and technology,2002(12/13):1633-1662. |
| [14] | K.I. Tserpes;P. Papanikos;G. Labeas;Sp. Pantelakis .Fatigue damage accumulation and residual strength assessment of CFRP laminates[J].Composite Structures,2004(2):219-230. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%