研究了钛加入量(质量分数分别为0.08％,0.12％,0.16％)对离心铸造法制备锌铝铜镁稀土合金显微组织和拉伸性能的影响.结果表明:先析出的η-Zn相以钛作异质形核点形核长大,钛的加入改变了锌铝铜镁稀土合金的凝固方式,钛还与铝形成Al2Ti和All+xTil-x相,分布在晶界上,抑制了共晶组织的生成;随钛加入量增大,合金的抗拉强度先降后升再降,而伸长率先升后降,当钛加入量为0.12％时,抗拉强度从310 MPa降到285MPa,但伸长率从加入前的4％提高到7％,提高了75％.
参考文献
| [1] | 关绍康,姚波,王迎新.Ti和Ce对AlMgSi基合金板材成形性能的影响[J].中国有色金属学报,2002(04):759-763. |
| [2] | Xiurong Zuo;Yuanwei Jing .Investigation of the age hardening behaviour of 6063 aluminium alloys refined with Ti, RE and B[J].Journal of Materials Processing Technology,2009(1):360-366. |
| [3] | SONG Min,CHEN Kanghua,HUANG Lanping.Effects of Ce and Ti on the microstructures and mechanical properties of an Al-Cu-Mg-Ag alloy[J].稀有金属（英文版）,2007(01):28-32. |
| [4] | 吕永刚.Al-Ti-B晶粒细化剂的组织与细化效果[J].航天制造技术,2009(01):30-32. |
| [5] | L. Lu;A.K. Dahle .Effects of combined additions of Sr and AlTiB grain refiners in hypoeutectic Al-Si foundry alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(0):288-296. |
| [6] | 李秀华,刘海峰,吕伟,刘震磊.Ce和Sr对压铸锌合金组织与力学性能的影响[J].金属热处理,2007(09):81-82. |
| [7] | 赵品,沈焕祥.B+Ti+Ce复合变质对ZA27合金组织与性能的影响[J].中国有色金属学报,2002(z1):232-235. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%