采用液态离子交换法制备了不同负载量的镍改性ZSM-5分子筛催化剂,并考察了上述催化剂的微观结构和物理化学特性及其在NH3-SCR反应中的催化性能。结果表明：在负载量〈10.9%时镍在分子筛中具有高度的分散性,而随着镍负载量的进一步增加,分子筛表面开始出现较大的NiO颗粒;镍元素只以＋2价存在于分子筛催化剂中;在NH_3-SCR反应中,镍负载量低于14.9%时,增加镍负载量将提高催化剂的低温活性;当反应温度超过300℃时,高温催化中心开始起作用,但随镍负载量的增加,高温活性开始下降时的温度逐渐降低。
Ni modified ZSM-5 zeolite catalysts with different nickel content were prepared using liquid ion-exchange method.The effects of nickel loading ratios on microstructure,physical-chemical characterization and selective catalytic reduction of NO_x with ammonia were investigated.The results showed that nickel species were finely dispersed on the ZSM-5 support with nickel content≤10.9%,the NiO particles began to appear on the surface of the zeolite catalysts with nickel loading ratio increasing;all of the nickel species in the zeolite catalyst is Ni～（＋2）;when the nickel loading was less than 14.9%,the activity of the catalysts at low temperature would increase with the nickel loading increasing in the NH3-SCR reaction;when the reaction temperature exceeded 300°C,high temperature catalytic center was activated,but with the continued increase of nickel loading,the temperature of high-temperature activity began to decline gradually reduced.
参考文献
| [1] | Qi GS;Yang RT .Selective catalytic oxidation (SCO) of ammonia to nitrogen over Fe/ZSM-5 catalysts[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2005(1):25-33. |
| [2] | Mourad Mhamdi;Sihem Khaddar-Zine;Abdelhamid Ghorbel .Influence of the cobalt salt precursors on the cobalt speciation and catalytic properties of H-ZSM-5 modified with cobalt by solid-state ion exchange reaction[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2009(1):42-50. |
| [3] | Mihaylov M;Hadjiivanov K .Redox couples in the selective catalytic reduction of NOx with hydrocarbons over Co-ZSM-5 and Ni-ZSM-5 catalysts: an FT-IR study[J].Chemical communications,2004(19):2200-2201. |
| [4] | Fudong Liu;Hong He;Yun Ding .Effect of manganese substitution on the structure and activity of iron titanate catalyst for the selective catalytic reduction of NO with NH3[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2009(1/2):194-204. |
| [5] | N.Sharma;K.M.Shaju;G.V.Subba Rao;B.V.R.Chowdari;Z.L.Dong;T.J.White .Carbon-Coated Nanophase CaMoO4 as Anode Material for Li Ion Batteries[J].Chemistry of Materials,2004(3):504-512. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%