通过三点弯曲蠕变试验,研究了聚丙烯木塑复合材料在23℃左右室内环境五种应力水平下的短期蠕变行为,并采用四元件模型对其蠕变行为进行模拟.依据时间-温度-应力等效原理,以5 MPa为参考应力水平,将其它四种应力水平下的蠕变曲线移位成5 MPa应力水平下的主曲线,从而可以预测聚丙烯木塑复合材料在5 MPa应力水平下大约3年内的蠕变行为.
参考文献
| [1] | Wood-plastic composites: current trends in materials and processing[J].Plastics, additives & compounding,2005(5):20,22-26-0. |
| [2] | M. BENGTSSON;K. OKSMAN .Silane crosslinked wood plastic composites: Processing and properties[J].Composites science and technology,2006(13):2177-2186. |
| [3] | Zhao YS;Wang KJ;Zhu FH;Xue P;Jia MY .Properties of poly(vinyl chloride)/wood flour/montmorillonite composites: Effects of coupling agents and layered silicate[J].Polymer Degradation and Stability,2006(12):2874-2883. |
| [4] | Nachtigall SMB;Cerveira GS;Rosa SML .New polymeric-coupling agent for polypropylene/wood-flour composites[J].Polymer Testing,2007(5):619-628. |
| [5] | 罗文波,安群力,杨挺青.非线性粘弹体的时间-温度-应力等效原理及其应用[J].固体力学学报,2001(03):219-224. |
| [6] | 罗文波,杨挺青,王霞瑜.高聚物自由体积与温度和应力水平的相关性[J].高分子材料科学与工程,2005(03):11-15. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%