采用金相、X射线衍射、扫描电镜和透射电镜等方法对两种不同Mn含量应变诱发孪晶(TWIP)钢拉伸前后的显微组织进行了研究.结果表明,Fe-15Mn-3Si-3Al钢的塑性增长机理主要是),γrcc→εhcp,γfcc→εhcp→αbcc相变诱发的TRIP效应;Fe-25Mn-3Si-3Al钢主要的塑性增长机制是孪晶诱发的TWIP效应.Fe-25Mn-3Si-3Al钢拉伸后有些奥氏体晶粒内存在两个或多个孪晶系统,孪晶界与原始奥氏体晶界都会阻碍孪晶的长大.层错能强烈影响TWIP钢的变形机制,随着Mn含量的增加,层错能不断增加,孪晶强化逐渐起主导作用.
参考文献
| [1] | Georg FROMMEYER;Udo BRUX;Peter NEUMANN .Supra-Ductile and High-Strength Manganese-TRIP/TWIP Steels for High Energy Absorption Purposes[J].ISIJ International,2003(3):438-446. |
| [2] | Steven Vereanunen;Bruno C;De Cooman et al.Microstructural evolution and crystallographic texture formation of cold rolled austenitic Fe-3OMn-3Al-3Si TW1P steel[J].Steel Research International,2003,6(74):370-375. |
| [3] | Grassel O;Kruger L;Frommeyer G et al.High strangth Fe-Mn-(Al,Si) TRIP/TWIPsteels development-properties-application[J].International Jounud of Plasticity,2000,16:1391. |
| [4] | 黄宝旭,王晓东,戎咏华,王利.TWIP钢研究的现状与展望[J].热处理,2005(04):4-6,11. |
| [5] | Sehramm R E;Reed R P .Stacking fauh energies of seven commercial austenitie stainless steels[J].Metallurgical and Materials Transactions,1975,6:1345-1351. |
| [6] | Venables J A.Deformation Twinning in fee Material[A].Reed-Hill,1963:77-116. |
| [7] | Ragharan K S;Sastri A S .Nature of the work-harding behavior in hadfield's manganese steel[J].Tran Met See AIME,1969,245:1569-1575. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%