介绍了一种新型化学镀镍工艺.分析了各单因素及组合方案对镀速、镀液稳定性及镀层性能的影响.结果表明,使用组合光亮剩的镀液镀速高,稳定性好,获得的镀层孔隙率低、耐蚀性好、硬度高.
A new electroless nickel plating process was introduced.The effects of individual affecting factor and combination scheme on the deposition rate,bath stability and deposit performance were analyzed.The results showed that the bath using combined brightener has high deposition rate and good stability and the deposit obtained thereof has low porosity,good corrosion resistance and high hardness.
参考文献
| [1] | 王憨鹰,陈焕铭,孙安,徐靖.光亮剂对化学镀镍磷合金镀层的影响[J].表面技术,2008(03):14-15,24. |
| [2] | 李宁;黎德育;屠振密.化学镀实用技术[M].北京:化学工业出版社,2003 |
| [3] | 徐瑞东,郭忠诚,朱晓云.新型光亮剂EN65D在化学镀Ni-P合金上的应用[J].表面技术,2001(06):19-21. |
| [4] | 徐瑞东,郭忠诚.新型化学镀镍光亮剂的研究[J].材料保护,2002(06):30-32. |
| [5] | 宋影伟,曲彦平,李德高.化学镀镍溶液光亮剂实验研究[J].表面技术,2002(03):21-24. |
| [6] | 黄鑫,贺子凯,蔡晓兰.中温酸性光亮化学镀镍[J].表面技术,2003(05):46-48. |
| [7] | 郑筱梅,李自林.全光亮化学镀镍液的组成优化及寿命研究[J].材料保护,2003(11):24-26. |
| [8] | 陈正法.现代镀镍光亮剂与中间体浅谈[J].材料保护,2007(03):78-79,82. |
| [9] | 刘峰.全光亮化学镀镍磷合金工艺研究[J].材料保护,2007(05):40-42. |
| [10] | 仵亚婷,汤义武,胡文彬,沈彬.化学镀镍液稳定性测试评估方法[J].电镀与环保,2004(02):27-29. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%