以Nd9.sFe76Zr3Co5B6.5合金为研究对象,研究了不同快淬速度(8～65 m/s)对合金的磁性能、交换耦合作用和微观结构的影响.结果表明,快淬速度对合金退火后的微观结构和磁性能具有显著地影响,适当的快淬速度将使合金退火后的晶粒细化、分布均匀,提高软、硬磁性相间的交换耦合作用,进而提高合金的磁性能.当淬速为15 m/s时,合金退火后具有最佳的综合磁性能:Br=0.976 T,Hcj=711.57 kA/m,(BH)max=150.61 kJ/m3.
参考文献
| [1] | Yang S.;Liu XS.;Li SD.;Xie GZ.;Song XP.;Gu BX.;Du YW. .Effect of wheel speed on the microstructure and exchange coupling interaction of nanocomposite Nd2Fe14B/alpha-Fe magnets[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):325-329. |
| [2] | AN Kang,HU Jifan,WANG Dongling,Qin Hongwei,Sun Guangfei,CHEN Jufang,YU Xiaojun,LI Bo.Effects of quenching speed and Joule heating on the magnetic properties of Nd9Fe86B5 ribbons[J].稀有金属（英文版）,2005(02):157-160. |
| [3] | 王占勇,周邦新,倪健森,徐晖,王现英,金鸣林,房永征.快淬速度对Nd2Fe14B/α-Fe纳米复合永磁材料结构和磁性能的影响[J].金属热处理,2008(06):28-31. |
| [4] | Kanekiyo H.;Hirosawa S. .Thick Fe3B/Nd2Fe14B nanocomposite permanent magnet flakes prepared by slow quenching[J].Journal of Applied Physics,1998(11 Pt.2):6265-6267. |
| [5] | 陈治安,罗骥,郭志猛.熔体快淬速度对Nd8 Fe73 Ti2 Zr2 B13.6 C1.4双相纳米晶永磁合金磁性能的影响[J].功能材料与器件学报,2010(03):255-260. |
| [6] | 韩瑞平,崔春翔,孙继兵,杨薇.快淬速度对Nd10Fe81Co3B6薄带相结构及晶化过程的影响[J].功能材料,2010(10):1741-1743. |
| [7] | 徐兴国,徐晖,谭晓华,满华,蔡平平,侯雪玲,倪建森.快淬速度对纳米晶复合Nd8.5Fe77.7Nb2Co5Ga0.6B6.2粘结永磁体温度系数的影响[J].稀有金属材料与工程,2011(08):1450-1453. |
| [8] | 高汝伟,代由勇,陈伟,章亚明,张茂才,乔纬,王佐诚,李卫,李岫梅,王玉山,罗军,Luo Jun.纳米晶复合永磁材料的交换耦合相互作用和磁性能[J].物理学进展,2001(02):131-156. |
| [9] | Kelly P.E.;O'Grady K. .Switching mechanisms in cobalt-phosphorus thin films[J].IEEE Transactions on Magnetics,1989(5):3881-3883. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%