The effects of surface state and applied stress on the stress corrosion cracking (SCC) behaviors of thermally treated (TT) Alloy 690 in 10 wt% NaOH solution with 100 mg/L litharge at 330 ℃ were investigated using C-ring samples with four kinds of surface states and two different stress levels. Sample outer surfaces of the first three kinds were ground to 400 grit (ground), shot-peened (SP) and electro-polished (EP) and the last one was used as the as-received state. Two samples of every kind were stressed to 100% and 200% yield stress of Alloy 690TT, respectively. The results showed that the oxide film consisted of three layers whereas continuous layer rich in Cr was not found. The poor adhesive ability indicated that the oxide film could not protect the matrix from further corrosion. Lead was found in the oxide film and the oxides at the crack paths and accelerated the dissolution of thermodynamically unstable Cr in these locations and also in the matrix. The crack initiation and propagation on Alloy 690TT were effectively retarded by SP and EP treatments but were enhanced by grinding treatment, compared with the cracks on the as-received surface. The cracking severity was also enhanced by increasing the externally applied stress. The accelerated dissolution of Cr and the local tensile stress concentration in the near-surface layer caused by cold-working and higher applied stress reduced the SCC-resistance of Alloy 690TT in the studied solution.
参考文献
| [1] | R.W. Staehle;J.A. Gorman .Quantitative Assessment of Submodes of Stress Corrosion Cracking on the Secondary Side of Steam Generator Tubing in Pressurized Water Reactors: Part 1[J].Corrosion: The Journal of Science and Engineering,2003(11):931-994. |
| [2] | S. Wang;Y. Takeda;K. Sakaguchi .Role of Work-Hardened Surface Layer in initiation of Environmentally Assisted Cracking in High-Temperature Water[J].Corrosion: The Journal of Science and Engineering,2006(8):651-656. |
| [3] | S. Wang;T. Shoji;N. Kawaguchi .Initiation of Environmentally Assisted Cracking in High-Temperature Water[J].Corrosion: The Journal of Science and Engineering,2005(2):137-144. |
| [4] | S. Le Hong .Influence of Surface Condition on Primary Water Stress Corrosion Cracking Initiation of Alloy 600[J].Corrosion: The Journal of Science and Engineering,2001(4):323-333. |
| [5] | F. Scenini;R.C. Newman;R.A. Cottis .Effect of Surface Preparation on Intergranular Stress Corrosion Cracking of Alloy 600 in Hydrogenated Steam[J].Corrosion: The Journal of Science and Engineering,2008(11):824-835. |
| [6] | N. Winzer;A. Atrens;W. Dietzel;G. Song;K.U. Kainer .Evaluation of the delayed hydride cracking mechanism for transgranular stress corrosion cracking of magnesium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):18-31. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%