A technology for recovering indium from Jinchuan copper-smelting ash was developed. Indium in the ash was first enriched to the leaching-slag in leaching process, and then recovered by sulfating roasting. The method included mixing the leaching-slag with sulfuric acid, making them into particles, roasting the mixture, and then leaching the calcine with hot water. Above 90% of indium in calcine could be dissolved into the leaching solution. The optimized conditions were determined as follows: the mass ratio of sulfuric acid to leaching slag was 0.1, the roasting time was about 1 to 1.5 h in the temperature range of 200-250 ℃, and the calcine was leached for 1 h with 5:1 of liquid/solid ratio at 60℃. Over 99% of indium in leaching solution was finally enriched by Zn substitution or sulfide precipitation.
参考文献
| [1] | 刘大春,杨斌,戴永年,杜国山,唐万启,韩龙.从富铟渣提取金属铟的研究[J].稀有金属,2005(04):574-577. |
| [2] | 周智华,莫红兵,徐国荣,唐安平.稀散金属铟富集与回收技术的研究进展[J].有色金属,2005(01):71-76,80. |
| [3] | Wang S C;Qi S Z.Resource Utility and Market of Indium[J].World Nonferrous Met,2000(12):22. |
| [4] | 俞小花,谢刚.有色冶金过程中铟的回收[J].有色金属（冶炼部分）,2006(01):37-39. |
| [5] | Zhang Q;Liang L J;Mai C X.The study of enriched zinc and indium from ash[J].Guangdong Eng,2004(04):33. |
| [6] | Guo T L;Li C J;Liu D Y.Production practice of indium metallurgy[J].Nonferrous Min Metall,2000(12):18. |
| [7] | Zhou L Y;Zou J Y.Rare Metal Manuals[M].长沙:中南大学出版社,1993:398. |
| [8] | Yang X Z .The development of spectrophotometric determination of indium[J].Chinese Journal of Rare Metals,1992,16(06):457. |
| [9] | Wei L Q;Xiao L X.Comprehensive utilization of indium-substitution liquid[J].Nonferrous Met Smelt,1999(04):29. |
| [10] | Guo T L;Ren Y M.The production of indium enriching during refining of zinc by wet method[J].Nonferrous Min Metall,1998(06):25. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%