含硅芳炔(PSA)树脂是一种新型耐高温树脂,固化后具有优良的力学性能和透波性.PSA树脂一般采用格氏试剂法制备,该方法制备的PSA(PSA-G)树脂固化后交联密度高,脆性较大.锌粉催化法是一种新型、高效的PSA合成方法.该方法合成的PSA(PSA-Zn)树脂末端含有部分烯键,树脂粘度低,交联密度小,脆性相对较小,但耐热性相对PSA-G树脂有所降低.采用PSA-G共混PSA-Zn得到改性树脂,研究了改性树脂的固化工艺、粘度、耐热性以及PSA-Zn质量分数为70％的改性树脂复合材料和树脂浇铸体的力学性能.研究结果表明PSA-Zn含量为70％的共混树脂粘度较低,为122mPa-s;热分解5％时的温度(Td5)达564℃,耐热性较好;复合材料具有良好的力学性能,浇铸体弯曲强度比PSA-G提高了11％.
参考文献
| [1] | 张玲玲;高飞;周围;张健;黄发荣;杜磊.含硅氢基团甲基芳炔树脂的合成及表征[J].过程工程学报,2009(3):574-579. |
| [2] | Itoh M.;Inoue K.;Hirayama N.;Sugimoto M.;Seguchi T..Fiber reinforced plastics using a new heat-resistant silicon based polymer[J].Journal of Materials Science,200217(17):3795-3801. |
| [3] | Zhang, J.;Huang, J.;Du, W.;Huang, F.;Du, L..Thermal stability of the copolymers of silicon-containing arylacetylene resin and acetylene-functional benzoxazine[J].Polymer Degradation and Stability,201112(12):2276-2283. |
| [4] | Zhen-yu Jiang;Yan Zhou;Fa-rong Huang;Lei Du.CHARACTERIZATION OF A MODIFIED SILICON-CONTAINING ARYLACETYLENE RESIN WITH POSS FUNCTIONALITY[J].高分子科学（英文版）,2011(06):726-731. |
| [5] | Itoh M.;Iwata K.;Mitsuzuka M.;Kakigano T.;Inoue K..NEW HIGHLY HEAT-RESISTANT POLYMERS CONTAINING SILICON - POLY(SILYLENEETHYNYLENEPHENYLENEETHYNYLENE)S[J].Macromolecules,19974(4):694-701. |
| [6] | Maeorg U.;Hagu H.;Verkruijsse HD.;Brandsma L.;Viirlaid S..On the in situ trimethylsilylation of zinc acetylides[J].Journal of Organometallic Chemistry,20002(2):341-342. |
| [7] | 严浩;齐会民;黄发荣.新颖含硅芳基多炔树脂的合成与性能[J].石油化工,2004(9):880-884. |
| [8] | Xu JF;Wang CY;Lai GQ;Shen YJ.Synthesis and characterization of phenylacetylene-terminated poly(silyleneethynylene-4,4 '-phenylethereneethynylene)s[J].European Polymer Journal,20072(2):668-672. |
| [9] | 沈浩;蒋孝杰;周燕;邓诗峰;杜磊;夏红娟;黄发荣.锌粉催化合成含硅芳炔树脂[J].过程工程学报,2014(2):329-334. |
| [10] | Wang MC;Zhao T.Polyarylacetylene blends with improved processability and high thermal stability[J].Journal of Applied Polymer Science,20075(5):2939-2946. |
| [11] | Wang, S.;Li, M.;Gu, Y.;Zhang, Z..Experimental study on crack defects formation in polyarylacetylene composites and modification improvement of resin[J].Journal of Composite Materials,201025(25):3017-3032. |
| [12] | Jianxiang Huang;Wei Du;Jian Zhang.Study on the copolymers of silicon-containing arylacetylene resin and acetylene-functional benzoxazine[J].Polymer bulletin,20092(2):127-138. |
| [13] | 汤乐旻;周燕;田鑫;邓诗峰;沈学宁;黄发荣;杜磊.改性含硅芳炔树脂及其复合材料性能研究[J].玻璃钢/复合材料,2012(6):41-46. |
| [14] | 齐会民,王光后,张健,高金淼,黄健翔,黄发荣,杜磊.含硅芳炔树脂的改性及其性能研究[C].第十五届全国复合材料学术会议论文集,2008:335-339. |
| [15] | 李晓杰;陈会高;袁荞龙;黄发荣.端乙炔基聚醚酰亚胺改性含硅芳炔树脂的性能[J].石油化工,2015(9):1115-1120. |
| [16] | 刘海帆;邓诗峰;黄发荣;杜磊.乙酰丙酮镍催化含硅芳炔树脂的固化反应行为[J].过程工程学报,2012(1):154-159. |
| [17] | 孙赛;刘木金;王海;崔天放.RTM成型工艺及其派生工艺[J].宇航材料工艺,2010(6):21-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%