采用两种方法优化EVA/TiO2纳米复合材料的制备方法与工艺参数,选取性能最佳的一步法制备样本,进一步应用FESEM方法表征纳米粒子的粒径及分散状态,并测试材料力学性能.研究发现,基于神经网络和遗传算法的优化方法比正交实验分析优化方法更佳;纳米TiO2微粒在EVA基体中分散良好,拉伸强度、断裂伸长率和弹性模量均有所提高,起到了增强增韧作用.纳米TiO2填充量为5%时,拉伸强度提高最多;纳米TiO2填充量为1%时,断裂伸长率提高最多;随着纳米TiO2填充量的增加,弹性模量整体呈上升趋势.
参考文献
| [1] | Ruckenstein E.;Yuan YM. .NANOCOMPOSITES OF RIGID POLYAMIDE DISPERSED IN FLEXIBLE VINYL POLYMER[J].Polymer: The International Journal for the Science and Technology of Polymers,1997(15):3855-3860. |
| [2] | Monserral Garcia;Werner E Van Zyl;Mattijs G J T C et al.[J].Industrial and Engineering Chemistry Research,2003,42:3750-3757. |
| [3] | 王宏岗.我国EVA的应用及市场分析[J].当代石油石化,2002(06):24-27. |
| [4] | Zanetti M;Camino G;Thomann R et al.[J].Polymer,2001,42:4501-4507. |
| [5] | Tang Y.;Hu YA.;Wang SF.;Gui Z.;Chen ZY.;Fan WC. .Preparation and flammability of ethylene-vinyl acetate copolymer/montmorillonite nanocomposites[J].Polymer Degradation and Stability,2002(3):555-559. |
| [6] | Qiul Z;Xie R C;Ding P et al.[J].Computers & Structures,2003,62:391-395. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%