采用球磨机对聚氯乙烯（PVC）进行力化学改性,讨论了处理前后PVC结构的变化。在此基础上,经热致相分离（TIPS）法制备了力化学改性前后所得PVC的平板膜,应用FT-IR、DSC和SEM等进行分析,讨论了所得膜的结构与性能。结果表明,力化学改性减少了导致PVC难以加工的石榴状结构,降低了PVC微晶的完善程度;经力化学改性PVC制得的TIPS法平板膜纯水通量可达693.6L/（m2.h）,较未经力化学改性PVC制得的TIPS法平板膜的水通量7.1L/（m2.h）有显著提高,膜的断裂强度也有所加强。
The mechanochemical treatment of PVC was studied by ball mill and the structure changes of PVC was analyzed.Based on the research,the flat membranes were prepared using the PVC before and after mechanochemical treatment,respectively by thermally induced phase separation(TIPS) method.The structure and properties of membranes were studied by FT-IR,DSC and SEM.Results showed that the mechanochemical treatment eliminated the PVC pomegranate appearance structure which made PVC difficult to be processed,and the perfection of initial micro-crystal of PVC was also reduced.The water flux of the flat membrane built of PVC after mechanochemical treatment by TIPS method reached 693.6L/(m2·h) which was much higher than that built of PVC before mechanochemical treatment with the value of only 7.1L/(m2·h),and the fracture strength of the flat membrane was also increased.
参考文献
| [1] | X. Y. Hu;Y. B. Chen;H. X. Liang .Preparation of polyurethane/poly(vinylidene fluoride) blend hollow fibre membrane using melt spinning and stretching[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2011(3):661-665. |
| [2] | Zhensheng Yang;Pingli Li;Lixin Xie;Zhi Wang;Shi-Chang Wang .Preparation of iPP hollow-fiber microporous membranes via thermally induced phase separation with co-solvents of DBP and DOP[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2006(1/3):168-181. |
| [3] | Mengxian Shang;Hideto Matsuyama;Masaaki Teramoto;Douglas R.Lloyd .Preparation and membrane performance of poly(ethylene-co-vinyl alcohol)hollow fiber membrane via thermally induced phase separation[J].Polymer: The International Journal for the Science and Technology of Polymers,2003(24):7441-7447. |
| [4] | Cha BJ;Yang JM .Preparation of poly(vinylidene fluoride) hollow fiber membranes for microfiltration using modified TIPS process[J].Journal of Membrane Science,2007(1/2):191-198. |
| [5] | 郭少云.力化学降解对聚氯乙烯加工流变行为的影响[J].高等学校化学学报,1994(08):1244. |
| [6] | 郭少云,徐僖.在应力作用下聚氯乙烯降解的研究[J].高分子材料科学与工程,1993(06):106-110. |
| [7] | Xu J;Xu Z L .Properties of PVC hollow fiber membranes and its prepared from PVC/additives/solvent[J].Journal of Membrane Science,2002,208(1-2):203-212. |
| [8] | Krim M S;Enomoto S .Infrared studies of conformation-al changes in polyvinyl chloride[J].Journal of Polymer Science Part A:Polymer Chemistry,1964,2(02):669-678. |
| [9] | Theodorou M;Jasse B .Fourier-transform infrared study of conformational changes in plasticized poly(viny[chlo-ride)[J].Journal of Polymer Science Part B:Polymer Physics,1983,21(11):2263-2274. |
| [10] | 黄志明,包永忠,翁志学.聚氯乙烯结晶行为研究[J].高分子材料科学与工程,1998(04):78-81. |
| [11] | 胡益林,刘俊龙,董跃.用差示扫描量热法优化PVC-U异型材加工工艺[J].塑料科技,2007(05):90-92. |
| [12] | 郑震.聚氯乙烯降解理论的进展[J].塑料,1999(03):8-14. |
| [13] | 金日光.高分子物理[M].北京:化学工业出版社,2007:76-77. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%