以间苯二酚-甲醛为原料,添加水溶性镍盐,利用溶胶-凝胶法制备了具有纳米多孔结构的掺镍碳气凝胶.通过X射线衍射及透射电镜表征了掺镍碳气凝胶的结构.用比表面积测试及孔径分布测试等手段研究了碳气凝胶的多孔特性,研究表明纯碳气凝胶的比表面积为487.3m2/g,掺杂后提高到593.3m2/g.掺镍碳气凝胶的电导率比未掺杂样品有很大的提高.
参考文献
| [1] | Pekala RW.;Alviso CT.;Tran TD.;Mayer ST.;Miller JM.;Dunn B.;Farmer JC. .Carbon aerogels for electrochemical applications[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):74-80. |
| [2] | Frackowiak E;Beguin E .Carbon material for the electrochemical storage of energy in capacitors[J].Carbon,2001,39:937. |
| [3] | Petricevic R;Glora M;Fricke J .Planar fibre reinforced carbon aerogels for application in PEM fuel cells[J].Carbon,2001,39:857. |
| [4] | 解德滨,沈军,吴广明,周斌,韩伟娜.炭气凝胶负极材料的制备及研究[J].电池,2006(04):302-304. |
| [5] | 薛辉,宓轶捷,罗爱云,沈军,吴广明,周斌.碳气凝胶的制备及其电除盐性能的研究[J].材料导报,2006(09):137-139. |
| [6] | 郭艳芝,沈军,陈绍国,周斌,王珏.惯性约束聚变靶材料碳气凝胶的制备方法[J].原子能科学技术,2002(04):324-326. |
| [7] | 秦仁喜,沈军,吴广明,周斌,王琴,倪星元,郭艳芝.碳气凝胶的常压干燥制备及结构控制[J].过程工程学报,2004(05):429-433. |
| [8] | 沈军,薛辉,吴广明,周斌.碳气凝胶的微结构控制[J].同济大学学报（自然科学版）,2007(06):779-782. |
| [9] | 张拴勤,王珏,沈军,周斌,朱基千,赖珍荃,陈玲燕.新型惯性约束聚变靶材料碳气凝胶研制[J].原子能科学技术,1999(04):305-308. |
| [10] | Maldonado-Hodar FJ.;Rivera-Utrilla J.;Hanzawa Y. Yamada Y.;Moreno-Castilla C. .Catalytic graphitization of carbon aerogels by transition metals[J].Langmuir: The ACS Journal of Surfaces and Colloids,2000(9):4367-4373. |
| [11] | Inagaki M.;Vignal V.;Konno H.;Oshida K.;Okada Y. .Graphite formation from a mixture of Fe3O4 and polyvinylchloride at 1000 degrees C[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(11):1706-1708. |
| [12] | Fu Ruowen;Theodore F Baumann;Steve Cronin et al.Formation of Graphitic Structures in Cobalt-and Nickel-Doped carbon aerogels[J].Langmuir,2005,21:2647. |
| [13] | 侯今强,沈军,薛辉,吴广明,周斌,倪星元.二氧化碳活化法制备高比表面积碳气凝胶[J].过程工程学报,2005(06):651-653. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%